热处理对铁素体不锈钢组织和性能的影响 预览 被引量:22

Effect of Heat Treatment Process on Microstructure and Properties of Ferrite Stainless Steel
在线阅读 下载PDF
收藏 分享 导出
摘要 研究了不同热处理工艺对铁素体不锈钢的组织与性能的影响.结果表明: 铁素体不锈钢固溶处理时,温度在900 ℃以下组织无明显变化,其硬度随着温度的上升变化缓慢;900 ℃左右发生再结晶,硬度显著降低;在475 ℃热处理后析出物增多,硬度增加,耐腐蚀性能严重下降,即有明显475 ℃脆性现象. Effect of heat treatment process on microstructure and mechanical properties of ferrite stainless steel was studied.The result shows that at the solid-solution temperature lower than 900 ℃,the microstructures of the steel do not change. With the temperature increasing,the hardness of the steel changes slowly.At the solid-solution temperature higher than 900 ℃,the recrystallization grain of the steel increases,the hardness decreases obviously.Aged at 475 ℃ for various time,the precipitates appear,the hardness of the steel increases and the corrosion resistance of the steel declines seriously.Such phenomena mentioned above is the 475 ℃ embrittlement of the steel.
作者 温军国 郑弃非 涂思京 赵云豪 李德富 Wen Junguo  Zheng Qifei  Tu Sijing  Zhao Yunhao  Li Defu  
出处 《稀有金属》 EI CAS CSCD 北大核心 2006年第z2期 152-154,共3页 Chinese Journal of Rare Metals
关键词 铁素体不锈钢 热处理 475℃脆性 ferrite stainless steel heat treatment 475℃ embrittlement
作者简介 温军国(1981-), 男, 四川资阳人, 硕士研究生 通讯联系人 (E-mail: guojun_@163.com)
  • 相关文献

参考文献10

二级参考文献4

  • 1Wang JIN, Jeom-Yong CHOI: ISIJ International, 1998,38 ( 7 ) :739-743. 被引量:1
  • 2Igor S. Golovin,Vladimir I. Sarrak,Svetlana O. Suvorova. Influence of carbon and nitrogen on solid solution decay[J] 1992,Metallurgical Transactions A(9):2567~2579 被引量:1
  • 3K. F. Ha,H. M. Zhang,K. L. Jing. An investigation on the mechanism of 475°C embrittlement in High-Cr ferritic stainless steel[J] 1989,Metallurgical Transactions A(11):2563~2567 被引量:1
  • 4林企曾,李成.转炉用铁水冶炼不锈钢的技术进展[J].不锈,2000(1):3-18. 被引量:3

共引文献88

同被引文献159

引证文献22

二级引证文献50

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈
新型冠状病毒肺炎防控与诊疗专栏