钛合金/不锈钢钎焊接头的组织特征 预览 被引量:7

Microstructural Characterization of Brazed Joints between Titanium and Stainless Steel
在线阅读 下载PDF
分享 导出
摘要 采用金相显微镜、电子显微镜、X射线能谱仪、显微硬度、力学试验等检测手段,对TA17钛合金/Ag95CuNiLi/0Cr18Ni10Ti不锈钢钎焊接头的组织特征进行了分析.结果表明:钎缝中不锈钢/钎料一侧,形成了三层金属间化合物钎缝组织;在钛合金/钎料一侧,形成两个组织区域;同时,银沿钛合金晶间扩散;在凝固钎焊接头的钎缝中,靠近不锈钢一侧出现了Ti、Cu的富集;靠近钛合金一侧Cu原子的含量明显升高,钎缝中心区基本上是纯银;钎缝中除不锈钢/钎料扩散层外,其他各微区的显微硬度并没有增加;从钎缝断口分析也证明钎缝中靠近不锈钢一侧是接头最薄弱的位置. Optical microscopy, scanning electron microscopy, EDXA, micro-hardness and mechanical properties tests were adopted to investigate the microstructural characterization of brazed joints between titanium alloy, Ag95CuNiLi and stainless steel. The results showed that three layers of inter-metallic compounds had formed at the side of stainless steel/filler metal, and two zones with different microstructures had been produced at the side of titanium alloy/filler metal. At the same time, Ag diffused along the grain boundary of titanium alloy. In brazed joints, Ti and Cu enriched at the side of stainless steel, and Cu enriched near the titanium alloy. The center area of the fillet is basically pure silver. Except that at the diffusion layer of the stainless steel/filler metal, the micro-hardness of other areas did not increase compared with the hardness before brazing. Joint failure analysis showed that the weakest occurred at the place near the stainless steel.
作者 杨静 朱常桂 王飞 朱金霞 刘晓荣 Yang Jing;Zhu ChangGui;Wang Fei;Zhu JinXia;Liu XiaoRong
出处 《核动力工程》 EI CAS 北大核心 2005年第4期 402-405,共4页 Nuclear Power Engineering
关键词 钛合金 不锈钢 钎焊接头 组织 Titanium alloy, Stainless steel, Brazed joint, Microstructural
作者简介 杨静(1967-),男,副研究员,2003年毕业于四川大学金属材料专业,获硕士学位现主要从事异性材料连接技术研究。 朱常桂(1950-),研究员:1976年毕业于清华大学核化工专业。现从事核燃料及材料研究。 王飞(1979-),实习研究员。2002年毕业于西南交通大学焊接专业,现主要从事异性材料连接技术研究。
  • 相关文献

参考文献4

二级参考文献9

共引文献22

同被引文献45

引证文献7

二级引证文献21

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈