耐热不锈钢管锈蚀原因分析 预览 被引量:1

ANALYSIS ON SURFACE CORROSION OF HEAT-RESISTANT STAINLESS STEEL TUBES
在线阅读 下载PDF
收藏 分享 导出
摘要 采用扫描电镜和X射线能谱分析等方法,对一批进口的耐热不锈钢管表面锈蚀原因进行了分析.结果表明,管子表面锈蚀是由海水浸入所致,同时该批管子部分焊缝区存在缩孔和裂纹等焊接缺陷,这些焊接缺陷降低了其耐腐蚀性能,从而加速了腐蚀过程的发生. Surface corrosion of heat-resistant stainless steel tubes imported was analyzed by SEM. EDS. It was shown that the surface corrosion on the tubes resulted from sea-water. And it was also shown that there were welding defects such as shrinkages and cracks. These defects lowered corrosion-resistant ability of the tubes, and accelerated the corrosion.
作者 曹标 林丽珍 谭莹 陈明 CAO Biao , LIN Li-zhen, TAN Ying , CHEN Ming (1. Guangzhou Entry-Exit Inspection and Quarantine Bureau, Guangzhou 510623, China; 2. Guangdong Power Industry School, Guangzhou 510520, China)
出处 《理化检验:物理分册》 CAS 2005年第10期 527-528,共2页 Physical Testing and Chemical Analysis Part A:Physical Testing
关键词 耐热不锈钢 表面锈蚀 原因分析 Heat-resistant stainless steel Surface corrosion Cause analysis
作者简介 曹标(1963-),男,高级工程师,博士.
  • 相关文献

参考文献3

  • 1化学工业部化工机械研究院.腐蚀与防护手册-腐蚀理论、试验及监测[M].北京:化学工业出版社,1995.. 被引量:1
  • 2黄建中,左禹主编..材料的耐蚀性和腐蚀数据[M].北京:化学工业出版社,2003:625.
  • 3毕洪运,于杰,赵鹏.G105钻杆腐蚀失效分析[J].理化检验:物理分册,2005,41(6):304-306. 被引量:10

二级参考文献2

共引文献9

同被引文献1

引证文献1

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈
新型冠状病毒肺炎防控与诊疗专栏