微量铌和钛对汽车扭杆用钢力学性能的影响 预览

Influence of Microalloying Elements Niobium and Titanium on the Mechanical Property of Steel for Torsion Bar of Automobile
在线阅读 下载PDF
收藏 分享 导出
摘要 本文研究了微合金化元素Nb、Ti对汽车扭杆用钢XC42P力学性能的影响。试验结果表明:以Nb和Ti微合金化可使XC42P钢的叮。平均提高约92MPa,σa/σb的值可达0、89以上;制成的扭杆在疲劳试验下,弹性退减全部小于0、5°。 This paper investigated the influence of microalloying elements niobium and titanium on the mechanical property of XCA2P, a kind of steel for torsion bar of automobile. The test results showed that microalloying with niobium and titanium could enhance cre of XCA2P by 92 MPa averagely with the ratio of σe to σb above 0, 89, The fatigue test of torsion bars showed that the elastic loss were smaller than 0.5 degrees,
作者 赵亚平 于平波 许斌 Zhao Yaping,Yu Pingbo,Xu Bin(1. Shanghai Jiaotong University, 2. Baoshan Iron & Steel Co. , Ltd. Special Steel Branch, Shanghai 200940, China)
出处 《上海钢研》 2006年第2期 35-38,共4页 Journal of Shanghai Iron and Steel Research
关键词 汽车用钢 扭力杆 微合金化 力学性能 steel for automobile torsion bar microalloying mechanical property