竹纤维抗紫外整理 预览 被引量:1

Anti-ultraviolet finish for bamboo fibers
在线阅读 免费下载
收藏 分享 导出
摘要 分别采用有机整理剂SCJ-966和无机整理剂TiO2对竹纤维织物进行抗紫外线整理,运用正交试验优化了抗紫外线整理工艺。结果表明,TiO2抗紫外处理后效果较佳,优化后的整理工艺为:TiO2 80g/L,Na2CO3 5g/L,160℃焙烘5min,整理后竹纤维紫外线透射率降低了68%。 Bamboo fiber fabric were finished using SCJ-966 and TiO2 anti-ultraviolet finishing agent separately. Factors affecting anti-ultraviolet results were optimized by orthogonal experiment. The results showed that TiO2 demonstrated the higher anti-ultraviolet performance than SCJ-966. The optimum process was TiO2 80 g/L,Na2CO3 5 g/L, curing at 160 ℃ for 5 minutes,the UV transmission rate of finished fabric decreased about 68% .
作者 陈志华 陈益人 CHEN Zhi-hua ,CHEN Yi-ren (1. Nantong Textile Vocational Technology College, Nantong 226007, China; 2.Textile & Material Institute, Wuhan University of Science And Engineering, Wuhan 430073, China)
出处 《印染》 北大核心 2009年第12期 35-36,共2页 Dyeing and Finishing
关键词 防辐射整理 紫外辐射 织物 竹纤维 radiation resistant finish ultraviolet radiation fabric bamboo fibers
作者简介 陈志华(1962-),男,江苏南通人,南通纺织职业技术学院副教授,苏州大学博士生.主要从事纺织品设计与纺织工艺的教学和研究。
  • 相关文献

同被引文献24

引证文献1

二级引证文献2

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈