电位极化方式对奥氏体不锈钢应力腐蚀开裂敏感性的影响

EFFECT OF POTENTIAL POLARIZATION ON THE STRESS CORROSION CRACKING OF AUSTENITIC STAINLESS STEEL
分享 导出
摘要 在慢应变速率拉伸过程中通过施加循环电位扫描及电位阶跃等不同的电位极化方式,研究了奥氏体不锈钢在酸性氯化物溶液中的应力腐蚀开裂敏感性,并利用SEM技术观察了断口形貌。结果表明,电位扫描速度和电位阶跃频率对裂纹萌生扩展起决定作用。相同电位范围内,电位阶跃比电位扫描导致更高的材料断裂敏感性。 The stress corrosion cracking susceptibility of 1Cr18Ni9Ti austenitic stainless steel in 0.75 mol·L -1 HCl+0.25 mol·L -1 NaCl solution has been studied by slow strain rate tests(SSRT).During the slow rate tensile process,the specimen was polarized with different potential polarization modes such as cyclic potential scan and cyclic potential step methods.The results indicated that potential scan rate and/or step frequency played an essential role in the initiation and propagation of crack.Potential step led to much higher cracking susceptibility than potential scan within the same potential ranges.
作者 牛林 林海潮 Niu Lin Zhang Zhenyu (School of Chem., Shandong Univ.,Jinan) Lin Haichao Cao Chunan (Inst. of Corrosion and Protection of Metals,Chinese Academy of Sciences, State Key Lab.for Corrosion and Protection.,Shenyang)
出处 《山东大学学报:自然科学版》 CSCD 1998年第4期 427-431,共5页 Journal of Shandong University(Natural Science Edition)
基金 国家自然科学基金,金属腐蚀与防护国家重点实验室资助
关键词 奥氏体不锈钢 应力腐蚀开裂 电位极化 敏感性 Austenitic stainless steel stress corrosion cracking potential polarization
  • 相关文献

参考文献3

  • 1张天成,金属学报,1997年,33卷,309页 被引量:1
  • 2金石(译),金属力学化学与腐蚀防护,1989年,2页 被引量:1
  • 3田昭武,电化学研究方法,1984年,204页 被引量:1
投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈