摘要 制备了一种新型含能胶凝剂羧甲基纤维素硝酸酯(CMCN),并将其制备成凝胶,用FTIR、TG和XRD分析了CMCN的结构、含氮量和热性能,研究了CMCN凝胶体系的流变性能。结果表明,与普通硝化纤维素相比,CM-CN的含氮量略低,初始分解温度在192℃左右,随着羧甲基含量的增加,CMCN的初始分解温度无变化,而最快分解温度增高,峰形变宽。CMCN凝胶体系具有良好的触变性。随着亲水性羧酸基团含量的增多,凝胶体系的强度和结构的稳定性提高,对外界的刺激响应逐渐减弱。 A new energetic gelator carboxymethyl cellulose nitrate(CMCN) was synthesized and its gel was prepared.The structure,nitrogen content and thermal properties of CMCN were analyzed by FTIR,TG and XRD,and rheology of CMCN gels was studied.The results show that the nitrogen content of CMCN is lower than normal NC and initial decomposition temperature of CMCNs is about 192℃.As the content of carboxymethyl increases,initial decomposition temperature of CMCNs has little change,but the fastest decomposition temperature increases and peak width broadenes.CMCN gel have good thixotropy.With increasing the content of hydrophilic carboxylic group,the strength and stability of gels increase,while the stimuli-responsive capability of gels decreases.
作者 吕少一 邵自强 王飞俊 张有德 张振玲 Lü Shao-yi,SHAO Zi-qiang,WANG Fei-jun,ZHANG You-de,ZHANG Zhen-ling(School of Materias Science and Engineering,Beijing Institute of Technology,Beijing 100081,China)
出处 《火炸药学报》 CAS CSCD 北大核心 2011年第1期 49-53,共5页 Chinese Journal of Explosives & Propellants
基金 燃烧与爆炸国防科技重点实验室基金(9140C3503011004)
关键词 材料科学 羧甲基纤维素硝酸酯 凝胶 流变性能 material science carboxymethyl cellulose nitrate gel rheological property
作者简介 吕少一(1983-),男,博士研究生,从事固体推进剂与天然高分子功能化研究。
  • 相关文献

参考文献13

二级参考文献97

共引文献62

同被引文献122

引证文献5

二级引证文献6

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈