波动载荷对C/C复合材料/铬青铜摩擦副载流摩擦磨损性能的影响 预览 被引量:8

Effects of Fluctuating Load on Friction and Wear Property of C/C Composite/QCr0. 5 under Electrical Current
在线阅读 下载PDF
分享 导出
摘要 借助于HST-100高速载流摩擦磨损试验机,研究载荷的波动大小对C/C复合材料/铬青铜摩擦副载流摩擦磨损性能的影响,利用扫描电镜对磨损表面进行观察分析。结果表明:随着载荷波动的加剧,平均电流逐渐减小,载流效率降低,离线率和电弧能量逐渐增大;C/C复合材料的摩擦因数和磨损率均呈现先减小然后增大的趋势;摩擦过程中的磨损机制逐渐由磨粒磨损转变为磨粒磨损、电气磨损共同作用。 The effects of fluctuating load on friction and wear property of C/C composite/QCrO. 5 under electrical current were studied on the HST-100 friction and wear testing machine with electrical current, and the worn surface of the sample was characterized by scanning electron microscope. The results show that with the increase of fluctuating load, the average current reduces, the current-carrying efficiency declines, the off-line rate and the arc energy increase. The friction coefficient and wear rate of C/C composite decreases at first and then increases, and the abrasion mechanism is abrasive wear, but with the increase of fluctuating load the abrasion mechanism becomes abrasive wear and electrical wear.
作者 田磊 孙乐民 赵燕霞 上官宝 张永振 Tian Lei,Sun Lemin,Zhao Yanxia,Shangguan Bao,Zhang Yongzhen (Institute of Materials Science and Engineering, Henan University of Science and Technology, Luoyang Henan 471003, China)
出处 《润滑与密封》 CAS CSCD 北大核心 2011年第11期 37-40,共4页 Lubrication Engineering
基金 国家973项目(2007EB607603) 国家自然科学基金项目(50975078) 973计划前期研究专项(2010CB635113) 国家重点联合基金项目(U1034002).
关键词 波动载荷 载流摩擦磨损 摩擦因数 磨损率 fluctuating load friction and wear with electrical current friction coefficient wear rate
作者简介 田磊(1986-),男,硕士研究生,目前主要从事材料干摩擦学研究.E-mail:tianlei0522311@163.com. 通讯作者:孙乐民(1965-),材料摩擦学方面研究.E-mail:男,博士,教授,目前主要从事sunlm@mail.haust.edu.cn.
  • 相关文献

参考文献8

二级参考文献16

共引文献33

同被引文献99

引证文献8

二级引证文献8

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈