控轧控冷工艺参数对冷镦钢10B21组织影响的热模拟研究 预览 被引量:2

Thermal Simulation Study of Effect of Controlling Rolling and Cooling Process Parameters on Structure of Cold Heading Steel 10B21
在线阅读 下载PDF
分享 导出
摘要 通过Gleeble-1500热模拟实验机对冷镦钢10821(/%:0.20C,0.02Si,0.85Mn,0.014P,0.005S,0.0018B)精轧前φ28mm圆坯进行控轧控冷工艺热模拟试验,以研究变形速率20s-1,变形艇65%时终轧温度(850~1000℃)、吐丝温度(820—940℃)和相变区冷却速度(0.2~1.0℃/s)对该钢组织的影响。结果表明,增加吐丝温度和相变区冷却速度可明显提高钢中铁素体含量,增加相变区冷却速度,可有效地改善钢的带状组织。为了获得较高的铁素体含量、粗大的铁素体晶粒且较均匀的组织,以提高钢的冷镦性能,较佳的控轧控冷工艺为终轧温度950℃、吐丝温度910℃、相变区冷却速度1.0℃/s。 Abstract The simulation test on controlling rolling and cooling process for ci)28 mm round billet of cold heading steel 10B21 (/% : 0. 20C, O. 20Si, 0. 85Mn, 0. 014P, O. 005S, 0. 001 8B) to be going to finishing rolling has been carried out by using Gleeble-1500 thermal simulation machine to study the effect of finishing rolling temperature- 850 - 1 000 ℃ with deformation rate 20 s- i and reduction- 65% , loop-laying temperature 820 -940℃ and cooling rate in phase transformation range- 0. 2 - 1.0 ℃/s on structure of steel. Results show that with increasing loop-laying temperature and cooling rate in phase transformation range the volume fraction of ferrite in steel increases obviously and with increasing cooling rate in phase transformation range the banded structure of steel is improved availably. In order to get higher ferrite volume fraction, coarser ferrite grain and more homogeneous structure to increase the cold heading performance, the optimum controlling roll- ing and cooling process parameters are finishing temperature- 950℃ , loop-laying temperature- 910 ℃ and eooling rate in phase transformation range- 1.0℃/s.
作者 蒋波 张朝磊 刘雅政 周乐育 Jiang Bo, Zhang Chaolei, Liu Yazheng and Zhou Leyu (School of Materials Science and Engineering, University of Science and Technology, Beijing 100083)
出处 《特殊钢》 北大核心 2014年第1期49-52,共4页 Special Steel
关键词 冷镦钢10B21 控轧控冷工艺参数 铁素体体积分数 铁素体平均晶粒尺寸 带状组织 Cold Heading Steel 10B21, Controlling Rolling and Cooling Process Parameter, Volume Fraction of Ferrite, Average Grain Size of Ferrite, Banded Structure
作者简介 蒋波(1990-),男,博士生(北京科技大学),2010年北京科技大学(本科)毕业,特殊钢变形工艺和组织性能的研究。
  • 相关文献

参考文献13

  • 1强十涌;乔德庸;李曼云.高速轧机线材生产[M]{H}北京:冶金工业出版社,2009. 被引量:1
  • 2孙维,华刚,许健,汪开忠.免退火高强度冷镦钢盘条SWRCH35K-M的研制[J].安徽工业大学学报:自然科学版,2007,24(1):25-28. 被引量:3
  • 3Elena P,Boyd J D. Effects of Simulated on Line Accelerated Cooling Processing on Transformation Temperatures and Microstructure in Microalloyed Steels[J].{H}Materials Science and Technology,1996,(12):1043-1052. 被引量:1
  • 4Hurley P J,Hodgson P D. Effect of Process Variables on Formation of Dynamic Strain Induced Ultrafine Ferrite during Hot Torsion Testing[J].{H}Materials Science and Technology,2001,(11):1360-1368. 被引量:1
  • 5田鹏 ,惠卫军 ,刘荣佩 ,张步海 ,于同仁 ,苏世怀 .形变参数对中碳钢组织演变的影响[J].材料热处理学报,2005,26(4):69-73. 被引量:14
  • 6Han D,Sun X J. Deformation Induced Ferrite Transformation in Low Carbon Steels[J].{H}Current Opinion in Solid State and Materials Science,2005,(06):269-276. 被引量:1
  • 7肖国华,王福明,李长荣,肖寄光.铌钒微合金化高强度船板钢的连续冷却转变规律[J].北京科技大学学报,2008,30(5):495-500. 被引量:11
  • 8Yuan W H,Fu Q,Zhou H. The Effect of Controlled Rolling and Cooling on the Microstructure Evolution of Boron Microalloyed Medium-carbon Steel[J].Advanced Materials Research,2011,(146-147):1305-1309. 被引量:1
  • 9许云波,刘相华,王国栋.奥氏体控轧控冷条件下相变后α晶粒尺寸的预测[J].东北大学学报:自然科学版,2002,23(2):144-147. 被引量:4
  • 10Ai J H,Zhao T C,Gao H J. Effect of Controlled Rolling and Cooling on the Microstructure and Mechanical Properties of 60Si2MnA Spring Steel Rod[J].{H}Journal of Materials Processing Technology,2005,(03):390-395.doi:10.1016/j.jmatprotec.2004.06.028. 被引量:1

二级参考文献49

共引文献57

同被引文献14

引证文献2

二级引证文献2

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈