Effect of three aging challenges on the bonding stability of resin-dentin interface using an etch-and-rinse adhesive
收藏 分享 导出
摘要 目的 比较3种老化方式对全酸蚀粘接系统牙本质粘接界面稳定性的影响,为树脂粘接剂的长期使用提供依据.方法 40颗离体人磨牙沿垂直于牙长轴的方向切割,暴露冠中部牙本质,用全酸蚀粘接系统(Single Bond 2)粘接处理后,堆积复合树脂,制备树脂-牙本质粘接试件.采用随机数字表法将样本牙分为4组(每组10颗):即刻对照组、唾液浸泡组、冷热循环组和细菌侵袭组.各组试件进行相应处理后,分别测试微拉伸强度,即粘接强度,使用扫描电镜和能量色散X射线光谱分析观察粘接界面的纳米渗漏情况.结果 3个老化组粘接强度均显著低于即刻对照组[(44.24±12.75) MPa,P <0.05],纳米渗漏分级均显著高于即刻对照组(P<0.05).细菌侵袭组粘接强度[(25.53±7.39) MPa]显著低于唾液浸泡组[(29.72 ±6.51) MPa]和冷热循环组[(31.92±11.87) MPa,P<0.05],后两组粘接强度差异无统计学意义(P>0.05).各老化组间纳米渗漏分级差异无统计学意义(P>0.05).结论 人工唾液浸泡、冷热循环和细菌侵袭3种老化方式均对全酸蚀粘接系统牙本质粘接界面的稳定性产生负面影响,细菌侵袭对界面稳定性的破坏作用最显著. Objective To systematically investigate the aging effect of thermocycling,water storage and bacteria aggression on the stability of resin-dentin bonds.Methods Forty molars were sectioned perpendicularly to the axis of the teeth to expose the middle-coronal dentin surfaces.The dentin surfaces were then treated with Single Bond 2 and made a core build-up.According to random digits table,the bonding specimens were divided into four groups (n =10)as follows:immediate control group,aging group with thermocycling for 5 000 times,aging group with artificial saliva storage for 6 months and aging group with bacteria aggression for 14 days.The specimens in each group were then subjected to microtensile bond strengths (μTBS) testing and nanoleakage evaluation respectively.Results After aging treatments,the three aging groups showed significantly lower μTBS than the immediate control group[(44.24 ± 12.75) MPa,P <0.05].The immediate control group also showed the lowest value of nanoleakage.The μTBS of aging group with bacteria aggression[(25.53 ± 7.39) MPa] was significantly lower than those of the other aging groups with artificial saliva storage [(29.72 ± 6.51) MPa] and thermocycling [(31.92 ± 11.87) MPa,P < 0.05].There were no differences in the nanoleakage values among the three aging groups(P >0.05).Conclusions All the aging treatments with artificial saliva storage,thermocycling and bacteria aggression could accelerate the degradation of bonding interfaces between an etch-and-rinse adhesive and dentin.Bacteria aggression showed the most impairing effect on the stability of resin-dentin bonds.
作者 徐帅 张凌 李芳 周唯 陈宇江 陈吉华 Xu Shuai,Zhang Ling,Li Fang,Zhou Wei,Chen Yujiang,Chen Jihua(Department of Prosthodontics, College of Stomatology, The Fourth Military Medical University, Xi'an 710032, China)
出处 《中华口腔医学杂志》 CAS CSCD 北大核心 2014年第6期367-370,共4页 Chinese Journal of Stomatology
基金 国家自然科学基金(51373198、81100772、81130078)
关键词 牙本质粘结剂 拉伸强度 老化 纳米渗漏 Dentin-bonding agents Tensile strength Aging Nanoleakage
作者简介 通信作者:张凌,Email:zhang.ling1978@gmail.com,电话:029-84776128
  • 相关文献

参考文献18

  • 1Breschi L, Mazzoni A, Ruggeri A, et al. Dental adhesion review : aging and stability of the bonded interface[ J]. Dent Mater,2008, 24(1) : 90-101. 被引量:1
  • 2Amaral FL, Colucci V, Palma-Dibb RG, et al. Assessment of in vitro methods used to promote adhesive interface degradation: a critical review[ J]. J Esthet Restor Dent,2007,19 (6) : 340-353. 被引量:1
  • 3Reis A, Grande RH, Oliveira GM, et al. A 2-year evaluation of moisture on microtensile bond strength and nanoleakage [ J ]. Dent Mater,2007,23 ( 7 ) : 862-870. 被引量:1
  • 4Osorio R, Pisani-Proenca J, Erhardt MC, et al. Resistance of ten contemporary adhesives to resin-dentine bond degradation [ J ]. J Dent,2008,36(2) : 163-169. 被引量:1
  • 5Pashley DH, Ciucchi B, Sano H, et al. Bond strength versus dentine structure : a modelling approach [ J ] . Arch Oral Biol, 1995,40(12) : 1109-1118. 被引量:1
  • 6陈宇江,刘宁,李芳,张凌,陈吉华.提高牙本质粘接界面稳定性的研究进展[J].中华口腔医学杂志,2013,48(2):119-122. 被引量:8
  • 7Yang B, Adelung R, Ludwig K, et al. Effect of structural change of collagen fibrils on the durability of dentin bonding [ J ]. Biomaterials ,2005,26 ( 24 ) : 5021-5031. 被引量:1
  • 8Giannini M, Seixas CA, Reis AF, et al. Six-month storage-time evaluation of one-bottle adhesive systems to dentin [ J ]. J Esthet Restor Dent ,2003,15 ( 1 ) : 43-48. 被引量:1
  • 9Tay FR,Hashimoto M,Pashley DH,et al. Aging affects two modes of nanoleakage expression in bonded dentin [ J]. J Dent Res,2003, 82(7) : 537-541. 被引量:1
  • 10Carrilho MR, Carvalho RM, Tay FR, et al. Durability of resin- dentin bonds related to water and oil storage [ J ]. Am J Dent, 2005,18(6) : 315-319. 被引量:1

二级参考文献40

  • 1Ferreira SQ,Costa TR,Klein-Junior CA. Improvement of exposure times:effects on adhesive properties and resin-dentin bond strengths of etch-and-rinse adhesives[J].Journal of Adhesive Dentistry,2011,(03):235-241. 被引量:1
  • 2Park J,Ye Q,Topp EM. Effect of photoinitiator system and water content on dynamic mechanical properties of a light-cured bisGMA/HEMA dental resin[J].Journal of Biomedical Materials Research Part A,2010,(04):1245-1251. 被引量:1
  • 3Ikemura K,Ichizawa K,Fuchigami K. Design of a new dental adhesive:effect of a water-soluble sodium acylphosphine oxide with crown ether on adhesion to dental hard tissues[J].Dental Materials,2009,(03):267-276. 被引量:1
  • 4Cadenaro M,Antoniolli F,Codan B. Influence of different initiators on the degree of conversion of experimental adhesive blends in relation to their hydrophilicity and solvent content[J].Dental Materials,2010,(04):288-294. 被引量:1
  • 5Miletic V,Santini A. Micro-Raman spectroscopic analysis of the degree of conversion of composite resins containing different initiators cured by polywave or monowave LED units[J].Journal of Dentistry,2012,(02):106-113. 被引量:1
  • 6Cadenaro M,Antoniolli F,Sauro S. Degree of conversion and permeability of dental adhesives[J].European Journal of Oral Sciences,2005,(06):525-530.doi:10.1111/j.1600-0722.2005.00251.x. 被引量:1
  • 7Kanca J 3rd. Resin bonding to wet substrate,1.Bonding to dentin[J].Quintessence International,1992,(01):39-41. 被引量:1
  • 8Tay FR,Pashley DH. Have dentin adhesives become too hydrophilic[J].Journal of the American Dental Association,2003,(11):726-731. 被引量:1
  • 9King NM,Tay FR,Pashley DH. Conversion of one-step to two-step self-etch adhesives for improved efficacy and extended application[J].American Journal of Dentistry,2005,(02):126-134. 被引量:1
  • 10Feitosa VP,Correr AB,Correr-Sobrinho L. Effect of a new method to simulate pulpal pressure on bond strength and nanoleakage of dental adhesives to dentin[J/OL].Journal of Adhesive Dentistry,2012. 被引量:1

共引文献7

同被引文献55

  • 1殷红,赵信义,何惠明,李江.不同病变程度氟斑牙牙本质对牙本质粘结剂粘结强度的比较研究[J].临床口腔医学杂志,2007,23(6):348-350. 被引量:3
  • 2Goldberg M,Kulkarni AB,Young M,et al.Dentin:structure,composition and mineralization[J].Front Biosci(Elite Ed),2011,3:711-735. 被引量:1
  • 3Ho SP,Sulyanto RM,Marshall SJ,et al.The cementum-dentin junction also contains glycosaminoglycans and collagen fibrils[J].J Struct Biol,2005,151(1):69-78. 被引量:1
  • 4Haruyama N,Sreenath TL,Suzuki S,et al.Genetic evidence for key roles of decorin and biglycan in dentin mineralization[J].Matrix Biol,2009,28(3):129-136. 被引量:1
  • 5Goldberg M,Septier D,Rapoport O,et al.Biglycan is a repressor of amelogenin expression and enamel formation:an emerging hypothesis[J].J Dent Res,2002,81(8):520-524. 被引量:1
  • 6Septier D,Hall RC,Embery G,et al.Immunoelectron microscopic visualization of pro-and secreted forms of decorin and biglycan in the predentin and during dentin formation in the rat incisor[J].Calcif Tissue Int,2001,69(1):38-45. 被引量:1
  • 7Milan AM,Sugars RV,Embery G,et al.Modulation of collagen fibrillogenesis by dentinal proteoglycans[J].Calcif Tissue Int,2005,76(2):127-135. 被引量:1
  • 8Bertassoni LE,Orgel JP,Antipova O,et al.The dentin organic matrix-limitations of restorative dentistry hidden on the nanometer scale[J].Acta Biomater,2012,8(7):2419-2433. 被引量:1
  • 9Orgel JP,Eid A,Antipova O,et al.Decorin core protein(decoron) shape complements collagen fibril surface structure and mediates its binding[J].PLoS One,2009,4(9):e7028. 被引量:1
  • 10Giachetti L,Bertini F,Scaminaci Russo D.Investigation into the nature of dentin resin tags:a scanning electron microscopic morphological analysis of demineralized bonded dentin[J].J Prosthet Dent,2004,92(3):233-238. 被引量:1

引证文献8

二级引证文献5

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈