38CrMoAl钢镗杆断裂原因分析

Analysis on breakage cause of 38CrMoAl steel boring bar
分享 导出
摘要 38CrMoAl镗杆在使用过程中突然断裂,从化学成分、显微组织、力学性能和冲击性能对其进行了分析。结果表明,钢的化学成分符合标准,镗杆为脆性断口,组织异常,冲击吸收能量很低,冲击断口也为脆性。断裂主要原因是镗杆有明显的上贝氏体组织,而且晶粒粗大。经分析是因加热温度高,冷却速度慢所致。提出了相应的改进措施。 A 38 CrMoAl steel boring bar was suddenly broken during service. The chemical composition,microstructure,mechanical properties and impact properties of the steel were investigated. The results show that the chemical composition meets the requirements,the fracture surface is brittle failure,microstructure is abnormal,and the impact energy is very low,and the impact fracture is also brittle one,which indicates that the main breaking reason is the upper bainite existing in the boring bar,and coarse grains,results from high austenitizing temperature and low cooling speed during quenching. The countermeasures are given according to this analysis result.
作者 张剑锋 左锦中 孟萌 卢明霞 Zhang Jianfeng, Zuo Jinzhong, Meng Meng, Lu Mingxia (Jiangyin Xingeheng Special Steel Co. , Ltd. , Jiangyin Jiangsu 214429, China)
出处 《金属热处理》 CAS CSCD 北大核心 2015年第7期193-195,共3页 Heat Treatment of Metals
关键词 38CRMOAL钢 樘杆 断裂 贝氏体 晶粒 38CrMoAl steel boring bar break bainite grain size
作者简介 张剑锋(1973-),男,学士,高级工程师,主要从事钢铁产品研发,发表论文12篇,联系电话:0510-80676903,E—mail:zhangjfjyxc@vip.sina.com
  • 相关文献

参考文献4

二级参考文献9

  • 1赵萍.快速渗氮工艺[J].金属热处理,1996(7):32-32. 被引量:10
  • 2王贮华 胡正琼.离子注入与分析基础[M].北京:航空工业出版社,1992.. 被引量:1
  • 3汪弘宏 田民波.离子束表面强化[M].北京:机械工业出版社,1992.. 被引量:1
  • 4B Josson and S Hogrnark. Thin solid Films[ M]. 1984. 被引量:1
  • 5汪弘宏 田民波.离子束表面强化[M].北京:机械工业出版社,1992.. 被引量:1
  • 6王贮华 胡正琼.离子注入与分析基础[M].北京:航空工业出版社,1992.. 被引量:1
  • 7夏立芳 高彩桥.钢的渗氮[M].北京:机械工业出版社,1989.. 被引量:43
  • 8克里乌林A B(田志敏译).钢与铸铁的硫碳氮共渗[M].北京:机械工业出版社,1982. 被引量:1
  • 9安运铮.热处理工艺学[M].北京:机械工业出版社,1998. 被引量:5

共引文献6

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈