屈曲模态对含缺陷复材加筋板后屈曲的影响 被引量:3

Effect of buckling mode on performance of post-buckled composite stringer-stiffened panels with debond
收藏 分享 导出
摘要 某些结构类型的复合材料加筋板,由于一阶和二阶屈曲载荷十分接近,在压缩失稳时,相同的试验件会出现不同的失稳模态,并表现出明显不同的后屈曲承载能力.就此问题,进行了试验和数值模拟研究.轴压试验中,通过影像云纹法和超声C扫技术监测试验件的失稳模态及缺陷扩展情况,以确定不同失稳模态对相同试验件后屈曲承载能力的影响.基于ABAQUS软件建立有限元模型,采用虚拟裂纹闭合技术(VCCT,Virtual Crack Closure Technology)模拟含预置脱胶缺陷的筋条-蒙皮界面,将失稳波形以几何扰动的形式引入后屈曲分析.通过分析缺陷前缘应变能释放率,研究两种模态下缺陷扩展特性.计算结果与试验结果相吻合,研究表明两种模态下缺陷的扩展特性明显不同,导致该型加筋板在3个半波失稳模态下的后屈曲承载能力明显高于2个半波模态下的后屈曲承载能力. Because of the proximity of first and second buckling load,some specific stringer-stiffened panels will exhibit different buckling modes under uniaxial compression load,which causes their post-buckling behavior strikingly different.Test and numerical calculation was conducted to study this phenomenon.Moiréinterferometry and ultrasonic scan were used to monitor the buckling mode and debond.Based on the software of ABAQUS,a finite element was developed.Virtual crack closure technology(VCCT) was used to simulate the interfaces with artificial debond.The initial geometric imperfection was led into model to process the nonlinear post-buckling analysis.By comparing the strain energy release rates of the crack front,the performance of debond propagation in two different modes was determined.The calculated results are coordinated with the tested results very well.The results indicate that the different damaging propagates under two buckling modes will generate that strength of panels with three half waves buckling mode exceeds the panels with two half waves buckling mode.
作者 徐荣章 关志东 刘璐 张楠 Xu Rongzhang;Guan Zhidong;Liu Lu;Zhang Nan;School of Aeronautic Science and Engineering,Beijing University of Aeronautics and Astronautics;The First Aircraft Design and Research Institute of China Aviation Industry;
出处 《北京航空航天大学学报》 EI CAS CSCD 北大核心 2014年第9期1299-1304,共6页 Journal of Beijing University of Aeronautics and Astronautics
关键词 复合材料加筋板 虚拟裂纹闭合技术(VCCT) 屈曲模态 缺陷扩展 后屈曲特性 composite stringer-stiffened panels virtual crack closure technology(VCCT) buckling mode damaging growth post-buckled
  • 相关文献

参考文献10

  • 1D.G. Stamatelos,G.N. Labeas,K.I. Tserpes.Analytical calculation of local buckling and post-buckling behavior of isotropic and orthotropic stiffened panels[J].Thin-Walled Structures.2010(3) 被引量:3
  • 2B.G Falzon,K.A Stevens,G.O Davies.Postbuckling behaviour of a blade-stiffened composite panel loaded in uniaxial compression[J].Composites Part A.2000(5) 被引量:1
  • 3R. Degenhardt,A. Kling,K. Rohwer,A.C. Orifici,R.S. Thomson.Design and analysis of stiffened composite panels including post-buckling and collapse[J].Computers and Structures.2007(9) 被引量:3
  • 4Se-Hee Oh,Kwang-Soo Kim,Chun-Gon Kim.An efficient postbuckling analysis technique for composite stiffened curved panels[J].Composite Structures.2005(3) 被引量:2
  • 5Hamid Reza Ovesy,Sayyed Amir Mahdi Ghannadpour,Ehsan Zia-Dehkordi.Buckling analysis of moderately thick composite plates and plate structures using an exact finite strip[J].Composite Structures.2013 被引量:1
  • 6Luca Lanzi.A numerical and experimental investigation on composite stiffened panels into post-buckling[J].Thin-Walled Structures.2004(12) 被引量:3
  • 7A.C. Orifici,S.A. Shah,I. Herszberg,A. Kotler,T. Weller.Failure analysis in postbuckled composite T-sections[J].Composite Structures.2008(1) 被引量:3
  • 8I.S. Raju,R. Sistla,T. Krishnamurthy.Fracture mechanics analyses for skin-stiffener debonding[J].Engineering Fracture Mechanics.1996(3) 被引量:1
  • 9Mark W Hilburger,James H Starnes.Effects of imperfections of the buckling response of composite shells[J].Thin-Walled Structures.2003(3) 被引量:2
  • 10杜善义,关志东.我国大型客机先进复合材料技术应对策略思考[J].复合材料学报,2008,25(1):1-10. 被引量:147

二级参考文献10

  • 1孙侠生,胡红东.国外民用飞机结构强度技术的发展思路研究[J].航空科学技术,2004(6):23-26. 被引量:8
  • 2胡红东,孙树栋.欧美加强民用航空复合材料技术开发[J].国际航空,2007(5):63-65. 被引量:2
  • 3Daly Kieran. So what next in the world of narrowbodies [EB/OL]. [2005-12-22]. http: //www. bizbuzzmedia. com/blogs/ flight_international/archive/2005 / 12/22/953. aspx. 被引量:1
  • 4Pora Jerome. Advanced Materials and Techanolgy for A380 Structure[J]. FAST Magazine, 2003, 32: 3-8. 被引量:1
  • 5Rosner H, Jockel-Miranda K. Airbus airframe new technologies and management aspects [J]. Materialwissenschaft und Werkstofftechnik, 2006, 37(9): 768-772. 被引量:1
  • 6Brosirus Dale. Boeing 787 update [EB/OL]. [2007-05]. http: // www. compositesworld. com/hpc/issues/2007/May/111535. 被引量:1
  • 7Shifrin Carole. 787: Expect something different [EB/OL]. [2005-06-20]. http: //www. aviationweek. com/aw/generic/ story_generic. jsp? channel= om&id= news/om605787. xml. 被引量:1
  • 8Wall Robert. Airbus relaunches A350 [EB/OL]. [2006- 12-10]. http: //www. aviationweek. com/aw/generic/story_generic. jsp? channel=awst&id=news/aw121106p3,xml. 被引量:1
  • 9Marsh George. Duelling with composites[J]. Reinforced Plastics, 2006, 50(6): 18-23. 被引量:1
  • 10Young Rick, Rohn Doug. Aviation safety program: Aircraft aging & durability project technical plan summary [EB/OL]. http ://www. aeronautics. nasa. gov/nra_ pdf/aad_ technical _ plan_cl, pdf_. 被引量:1

共引文献151

同被引文献15

引证文献3

二级引证文献4

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈
新型冠状病毒肺炎防控与诊疗专栏