热处理与应力集中对Q345R钢磁记忆检测结果的影响 被引量:3

Effect of heat treatment and stress concentration on magnetic memory signal in Q345R steel
分享 导出
摘要 通过磁学分析和磁记忆检测,研究了应力集中和去应力热处理对磁记忆检测结果的影响。结果表明:热处理前,应力集中和缺陷尺寸共同影响磁记忆信号的变化;缺陷引起磁记忆信号发生明显变化,并且磁记忆信号随着缺陷尺寸的增加表现出线性增加的规律。试样经过去应力热处理后,磁记忆信号明显削弱,难以反应出缺陷的位置。在外载荷作用下,磁记忆信号随着外加载荷的增加呈现出指数递增的变化规律。因此,应用磁记忆检测技术进行无损检测应充分考虑被测对象热处理状态和外加载荷的影响。并且,金属磁记忆检测结果可以用来验证去应力热处理的效果。 Effect of stress concentration and stress relief heat treatment( SRHT) on magnetic memory testing results of Q345 R steel was studied by means of magnetic analysis and magnetic memory testing. The results show that before SRHT,the changes of magnetic memory signals are affected by the stress concentration and the size of the defect,and the defect effect is significantly,and it shows a linearly increases with increasing the size of the defect. However,after SRHT,the magnetic memory signal of the specimen becomes weaker and does not clearly reflect the position of the defect due to the relief of stress concentration in defect area. When the loads are applied to specimen,the magnetic memory signal of defective area shows an exponentially increasing relationship with increase of stress. Therefore,the SRHT and the applied loads can be considered in the application of magnetic memory testing technology. Also,metal magnetic memory test results can be used to verify the effect of SRHT.
作者 徐坤山 仇性启 刘靖涛 陈长标 魏仁超 XU Kun-shan, QIU Xing-qi, LIU Jing-tao , CHEN Chang-biao, WEI Ren-chao (1. Institute of Chemical Engineering, China University of Petroleum (East China), Qingdao 266580, China; 2. Shandong QILU Petrochemical Construction LTD, Zibo 255400, China; 3. Zibo Branch of Shandong Special Equipment Inspection and Research Institute, Zibo 255086, China)
出处 《材料热处理学报》 EI CAS CSCD 北大核心 2016年第5期210-215,共6页 Transactions of Materials and Heat Treatment
基金 国家“863”计划课题(2013AA092602) 山东省质监系统科技计划项目(2015KY21)
关键词 缺陷 热处理 应力集中 磁记忆 defect heat treatment stress concentration magnetic memory
作者简介 作者简介:徐坤山(1981-),男,博士研究生,主要研究方向为承压设备安全与无损检澳0,发表论文10余篇,电话:13969314701,E-mail:17911162@qq.com。 通讯作者:仇性启(1956-),男,教授,博士,电话:0532-86983523,E—mail:apvshi@upc.edu.cn。
  • 相关文献

参考文献13

  • 1Dubov A A.A study of metal properties using the method of magnetic memory[J].Metal Science and Heat Treatment,1998,39(9):401-405. 被引量:1
  • 2Dubov A A.Development of a metal magnetic memory method[J].Chemical and Petroleum Engineering,2012,47(11):837-839. 被引量:1
  • 3Maciej Roskosz,MichaL Bieniek.Evaluation of residual stress in ferromagnetic steels based on residual magnetic field measurements[J].NDT&E International,2012(45):55-62. 被引量:1
  • 4Maciej Roskosz,MichaL Bieniek.Analysis of the universality of the residual stress evaluation method based on residual magnetic field measurements[J].NDT&E International,2013(54):63-68. 被引量:1
  • 5Roskosz M,Rusin A,Kotowicz J.The metal magnetic memory method in the diagnostics of power machinery components[J].Journal of Achievements in Materials and Manufacturing Engineering,2010,43(1):362-370. 被引量:1
  • 6Maciej Roskosz.Metal magnetic memory testing of welded joints of ferritic and austenitic steels[J].NDT&E International,2011(44):305-310. 被引量:1
  • 7Liu B,Fu Y,Xu B.Study on metal magnetic memory testing mechanism[J].Research in Nondestructive Evaluation,2015,26(1):1-12. 被引量:1
  • 8Anatoly Dubov,Sergey Kolokolnikov.The metal magnetic memory application for online monitoring of damage development in steel pipes and welded joint specimens[J].Weld Word,2013(57):123-136. 被引量:1
  • 9Wang Z D,Yao K,Deng B,et al.Quantitative study of metal magnetic memory signal versus local stress concentration[J].NDT&E International,2010(43):513-518. 被引量:1
  • 10Yao K,Wang Z D,Deng B,et al.Experimental research on metal magnetic memory method[J].Experimental Mechanics,2012(52):305-314. 被引量:1

二级参考文献9

  • 1Atherton D L.Magnetic inspection is key to ensuring safe pipelines[J].Oil Gas J,1985,87 (32):52-61. 被引量:1
  • 2Jiles D C.Review of magnetic methods for nondestructive evaluation (Part 2)[J].NDT International,1990,23(2):83-92. 被引量:1
  • 3Shcherbinin V E,Pashagin A I.Influence of the extension of a defect on the magnitude of its magnetic field[J].Defektoskopiya,1972,8 (4):441-447. 被引量:1
  • 4Foerster F.New findings in the field of nondestructive magnetic leakage field inspection[J].NDT International,1986,19(1):3-14. 被引量:1
  • 5Edwards C,Palmer S B.The magnetic leakage field of surface-breaking cracks[J].Appl Phys,1986,19(4):657-673. 被引量:1
  • 6Minkov D,Takeda Y,Shoji T,et al.Estimating the sizes of surface cracks based on Hall element measurements of the leakage magnetic field and a dipole model of a crack[J].Appl Phys,2002,74(2):169-176. 被引量:1
  • 7Hwang J H,Lord W.Finite element modeling of magnetic field/defect interactions[J].Journal of Testing & Evaluation,1975,3(1):21-25. 被引量:1
  • 8Ichizo Uetake,Tetsuya Saito.Magnetic flux leakage by adjacent parallel surface slots[J].NDT&E International,1997,30 (6):371-376. 被引量:1
  • 9Mandal K,Atherton D L.A study of magnetic flux-leakage signals[J].Appl Phys,1998,31:3211-3217. 被引量:1

共引文献6

同被引文献23

引证文献3

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈