超声波对电沉积Pd-Ni-P合金的影响 被引量:1

InfluencesofUltrasound on Process of Electrodeposited Pd-Ni-P Alloy and Film Performance
在线阅读 下载PDF
收藏 分享 导出
摘要 合金电镀应用广泛,但将超声波用于合金电镀的研究还不系统。以超声波与电沉积相结合制备Pd-Ni-P合金,通过扫描电镜(SEM)、能谱仪(EDX)、X射线衍射仪(XRD)等对Pd-Ni-P合金镀层的形貌、成分和组织结构进行了表征,采用循环伏安法研究了超声波对Pd-Ni-P合金电沉积的影响。结果表明:超声波作用使沉积层中Pd的含量增加,镀层表面更致密均匀;超声波振荡有利于溶液中离子的传质过程,主要是提高了Pd^2+的沉积速率;在1.0mol/LNaOH溶液中,超声波作用显著增强了Pd.Ni-P合金镀层的耐腐蚀性能,使腐蚀电位正移80mV。 Pd-Ni-P alloy film was prepared by electrodeposition technology under ultrasonic condition.Subsequently,scanning electron microscope(SEM),energy dispersive spectrometer(EDX) and X-ray diffractometer(XRD) were used to characterize the morphology,composition and structure of Pd-Ni-P alloy film.Results showed that the ultrasound caused the increase of Pd content in deposition layer,and the surface of film became more uniform.Moreover,the ultrasonic oscillation was beneficient to the mass-transfer process of ions in solution,and improved the deposition rate of Pd~(2+).In1.0 mol/L NaOH solution,the ultrasonic effect significantly enhanced the corrosion resistance of Pd-Ni-P alloy film,and the corrosion potential was shifted by 80 mV.
作者 周颖华 牛振江 ZHOU Ying-hua;NIU Zhen-jiang;Zhejiang Key Laboratory for Reactive Chemistry on Solid Surfaces-Institute of Physical Chemistry,Zhejiang Normal University;Zhejiang Jinhua Education College
出处 《材料保护》 CAS CSCD 北大核心 2016年第7期35-37,共3页 Journal of Materials Protection
关键词 Pd-Ni-P合金 电沉积 超声波 循环伏安法 XRD SEM EDX 耐腐蚀性 Pd-Ni-P alloy electrodeposition ultrasound cyclic vnltammetry XRD SEM EDX corrosion resistance
  • 相关文献

参考文献11

二级参考文献70

共引文献18

同被引文献9

引证文献1

二级引证文献2

论文智能改写系统
维普数据出版直通车
投稿分析
职称考试

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈