钛表面电火花沉积涂层的微观特征及性能 预览 被引量:1

Microstructure and Properties of Electrodeposited Coatings on Titanium Surface
在线阅读 免费下载
分享 导出
摘要 在TA2基体表面电火花沉积制备WC涂层和CoCr/WC涂层,对比研究两种涂层的形貌、表面粗糙度、厚度、物相组成、显微硬度以及相对耐磨性。研究结果表明:CoCr/WC涂层比WC涂层缺陷少,界面结合较好。WC涂层和CoCr/WC涂层表面粗糙度分别约为7.887μm和7.445μm。WC涂层和CoCr/WC涂层厚度分别约为20μm和40μm。WC涂层表面主要由W_2C、TiC和W等物相组成,CoCr/WC涂层表面主要由W_2C、Co_3W_3C和W等物相组成。WC涂层表面和CoCr/WC涂层表面显微硬度值最大分别达970HV和1040HV。WC涂层和CoCr/WC涂层的相对耐磨性分别为2.5和3.2。制备WC涂层和CoCr/WC涂层使基体表面性能发生改变,CoCr/WC涂层的综合性能优于WC涂层。 WC coating and CoCr/WC coating were prepared on the surface of TA2 basis material by electro spark deposition. The morphology,surface roughness,thickness,phase composition,microhardness and relative wear resistance of the two coatings were compared. The results show that the CoCr/WC coating has fewer defects and better interfacial bonding than WC coating. The surface roughness of WC coating and CoCr/WC coating is about 7. 887 μm and 7. 445 μm,respectively. The thickness of WC coating and CoCr/WC coating is about 20 μm and 40 μm respectively. The surface of WC coating is mainly composed of W_2C,TiC and W. The CoCr/WC coating is mainly composed of W_2C,Co_3W_3C and W. The highest microhardness of WC coating surface is 970 HV,and the highest microhardness of CoCr/WC coating is 1 040 HV. The relative wear resistance of WC coating and CoCr/WC coating is respectively 2. 5 and 3. 2. WC coating and CoCr/WC coating make the surface properties of the substrate change,and the comprehensive performance of CoCr/WC coating is better than that of WC coating.
作者 吴公一 于华 张占领 邱然锋 张柯柯 WU Gongyi;YU Hua;ZHANG Zhanling;QIU Ranfeng;ZHANG Keke;Materials Science &Engineering School,Henan University of Science & Technology;Collaborative Innovation Center of Non-ferrous Metals of Henan Province,Henan University of Science & Technology;
出处 《河南科技大学学报:自然科学版》 北大核心 2017年第5期11-15,共5页 Journal of Henan University of Science & Technology:Natural Science
基金 国家自然科学基金项目(U1294520) 河南省杰出青年科学基金项目(074100510011)
关键词 TA2 WC COCR 电火花沉积 复合涂层 界面行为 性能 TA2 WC CoCr ectro-spark deposition composite coating interface behavior property
作者简介 吴公一(1991一),男,河南南阳人,硕士生; 于华(1972一),女,通信作者,河南商丘人,副教授,硕士,硕士生导师,主要从事先进材料连接及材料表面改性研究.
  • 相关文献

参考文献11

二级参考文献129

共引文献64

同被引文献11

引证文献1

二级引证文献1

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈