120 t RH自然脱碳精炼低碳钢QD08的生产实践 预览

Production Practice for Low Carbon Steel QD08 Steelmaking by Natural Decarburization during 120 t RH Refining Process
在线阅读 下载PDF
分享 导出
摘要 基于生产数据对120 t RH精炼低碳钢QD08(/%:≤0.07C,0.15~0.35Si,0.25~0.45Mn,≤0.035P,≤0.035S)进行了RH碳氧反应的热力学、动力学分析和自然脱碳分析,得出RH精炼自然脱碳的优化工艺。结果表明,BOF终点温度≥1650℃,RH初始温度≥1 600℃,BOF终点[C]0.04%~0.10%,[P]≤0.018%,出钢前加顶浇石灰200 kg,出钢不加合金和脱氧剂,RH真空度4~8 kPa,6~8 min可使钢水[C]≤0.05%。 Based on the production data the analysis on thermodynamics, kinetics of RH carbon-oxygen reaction and natural decarburization in 120 t RH refining process of low carbon steel QD08 (/% :≤0.07C, 0. 15 ~0. 35Si, 0.25 ~ 0. 45Mn, ≤0. 035P, ≤0. 035S) has been carried out to get the optimized process for RH refining natural decarburization. The results show that with BOF end temperature ≥1 650 ℃, RH initial temperature of liquid ≥ 1 600 ℃, BOF end [ C ] 0. 04% ~ 0. 10%, end [ P] ≤0. 018%, before BOF tapping adding top slag lime 200 kg and during tapping non-adding alloy and deoxidation agent, and RH vacuum 4 -8 kPa for 6 ~ 8 min, the liquid [ C] shall decrease to ≤0. 05%.
作者 李海 刘列喜 张洪彪 介瑞华 王立青 陆曼 徐雷 Li Hai, Liu Liexi, Zhang Hongbiao, Jie Ruihua, Wang Liqing, Lu Man and Xu Lei (Steelmaking Division, Wuhu Xinxing Casting Pipe Co Ltd, Wuhu 241000)
出处 《特殊钢》 北大核心 2018年第3期13-16,共4页 Special Steel
关键词 QD08低碳钢 RH精炼 自然脱碳 热力学 脱碳速率 Low Carbon Steel QD08, RH Refining, Natural Decarburization, Thermodynamics, Decarburization Rate
作者简介 李海(1985-),男,硕士(2012年内蒙古科技大学),工程师,2008年内蒙古科技大学(本科)毕业,二次精炼研究和品种开发。
  • 相关文献

参考文献6

二级参考文献45

共引文献31

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈