Al/Zn双金属复合板的界面研究

Interface of Al/Zn Bimetal Composite Plate
分享 导出
摘要 采用复合铸造制备了A356/Zn双金属复合板。通过改变两种合金的浇注顺序和A356铝合金浇注温度来改变复合板界面组织和过渡区厚度。通过对复合界面进行SEM+EDS分析,研究了A356/Zn双金属复合板界面组织的形成机制。结果表明,当A356铝合金浇注温度为660℃时,界面实现了良好的冶金结合,形成了发达的树枝晶,过渡区厚度约为2mm,结合界面根据生成相的不同可以分为3个区域;当A356铝合金的浇注温度为620℃时,中间区域的树枝晶有明显减小甚至消失,过渡区的厚度减小到约1mm。 A356/Zn bimetal composite plate was prepared by double liquid composite casting.The interfacial microstructure and interface cross sectional height of the composite plate were adjusted by changing the pouring sequence of the two alloys and the pouring temperature of A356 aluminum alloy.The microstructure and mechanism of composite layer formation at the A356/Zn interface were evaluated by scanning electron microscope(SEM)and energy dispersive spectrometer(EDS).The results reveal that the interface of A356/Zn bimetal composite plate presents desirable metallurgical bonding with A356 melt at660 ℃,where a well-developed dendrite can be formed with interface cross sectional height of about 2 mm.The interface can be divided into three regions based on the generation phase.When the pouring temperature of A356 aluminum alloy is 620℃,the dendrites in the composite interface are reduced obviously or even absent with the width of composite interface decreased to about 1 mm.
作者 孙延蓝 李元东 蒋春宏 陈天赐 李明 毕广利 Sun Yanlan, Li Yuandong1,2,Jiang Chunhong3,Chen Tianci ,Li Ming ,Bi Guangli1,2 (1.State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology; 2. Key Laboratory of Non-ferrous Metal Alloys, the Ministry of Education, Lanzhou University of Technology; 3.Lanzhou Lanshi Detection Technology Co., Ltd.)
出处 《特种铸造及有色合金》 CSCD 北大核心 2018年第5期535-539,共5页 Special Casting & Nonferrous Alloys
基金 国家自然科学基金资助项目(51464031) 甘肃省重点研发计划资助项目(17YF1GA021)
关键词 A356/Zn双金属 界面组织 元素扩散 形成机制 A356/Zn Bimetal Composite Plate Interfacial Microstructure Element Diffusion Formation Mechansim
作者简介 孙延蓝,男,1992年出生,硕士研究生,兰州理工大学省部共建有色金属先进加工与再利用国家重点实验室,兰州(730050),电话:18793168324,E-mail:1352736715@qq.com;通信作者:李元东,男,1971年出生,教授,兰州理工大学省部共建有色金属先进加工与再利用国家重点实验室,兰州(730050),电话:0931-2976795,E-mail:liyd_lut@163.com
  • 相关文献

参考文献10

二级参考文献170

共引文献119

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈