电渣重熔1Cr13钢中夹杂物的研究 预览

Study of Inclusion of 1Cr13 Steel Forging by Electro Slag Remelting
在线阅读 下载PDF
分享 导出
摘要 采用蔡司金相显微镜、扫描电镜和能谱分析等检测手段表征了1Cr13钢锻件内夹杂物的元素组成和形态。结果表明,电渣重熔1Cr13钢锻件内夹杂物的主要元素有Mn、F、S、Si、O和Ca,其中F、Si、Ca含量严重超标,S和O含量轻微超标,Mn含量在标准范围之内。由此确定1Cr13钢夹杂物的存在形态为块状Si O2和条状Mn S两类夹杂物,而Ca F2是以夹渣形式出现。 Element composition and morphology of inclusion of 1 Cr13 steel forging were characterized by OM, SEM and EDS. The results show that essential elements of inclusion are Mn, F, S, Si, O and Ca in the 1 Cr13 steel forging. The contents of F, Si and Ca are the severe over-standard, and the contents of S and O are the minor over-standard, and the content of Mn is within range of standard. From that, the existing forms of inclusion are blocks of Si O2 and strips of Mn S, and Ca F2 comes out in slag inclusion.
作者 霍宝阳 赵作福 莫梓睿 张晓盼 齐锦刚 HUO Bao-yang, ZHAO Zuo-fu, Mo Zi-rui, ZHANG Xiao-pan, QI Jin-gang ( School of Materials Science and Engineering, Liaoning University of Technology, Jinzhou 121001, China )
出处 《辽宁工业大学学报:自然科学版》 2018年第3期192-195,共4页 Journal of Liaoning Institute of Technology(Natural Science Edition)
基金 国家自然科学基金(51601086) 辽宁省教育厅高等学校重大科技平台科学技术研究项目(JP2017013) 辽宁省教育厅高校基本科研项目(JQL201715407) 辽宁省科技厅项目(2017105007)
关键词 电渣重熔 1Cr13 夹渣 锻件 ESR (electro slag remelting) 1Cr13 slag inclusion forging
作者简介 霍宝阳(1995-),男,辽宁朝阳人,本科生。;赵作福(1978-),男,辽宁锦州人,高级实验师,博士。
  • 相关文献

参考文献10

二级参考文献106

共引文献99

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈