SEBS改性磺化沥青性能的研究 预览

Study on the properties of SEBS modified sulfonated asphalt
在线阅读 下载PDF
收藏 分享 导出
摘要 通过向建筑沥青中加入SEBS磺化得到改性磺化沥青,研究了磺化剂用量对磺化沥青降滤失性能的影响。并对磺化沥青进行了扫描电镜、Zeta电位、降滤失性能及配伍性研究。结果表明,当SEBS加量为5%,磺化比为1∶0.7时,高温高压滤失量达到24mL,高温高压滤失量降低率达到55.56%,具有良好的降滤失性能;改性后的磺化沥青具有较好的配伍性,当样品加量达到2%,高温高压滤失量降低率达到了45.45%,说明改性磺化沥青具有良好的封堵性能。 The construction asphalt modified with SEBS was sulfonated,and the effect of the amount of sulfonation agent on the loss-reduction performance of sulfonated asphalt was studied.The sulfonated asphalt was studied by scanning electron microscopy,Zeta potential,filtration loss performance and compatibility.The results show that when the amount of SEBS is 5%and the sulfonation ratio is 1∶0.7,the filtration loss of high temperature and high pressure reaches 24 mL,and the reduction rate of high temperature and high pressure filtration loss reaches 55.56%,the modified sulfonated asphalt has good compatibility.When the sample amount reached 2%,the high temperature and high pressure filtration loss reduction rate reaches 45.45%,indicating that the modified sulfonated asphalt has good sealing performance.
作者 胡正文 孟义征 邓小刚 马丽华 林凌 彭玉凤 姜雄 HU Zheng-wen;MENG Yi-zheng;DENG Xiao-gang;MA Li-hua;LIN Ling;PENG Yu-feng;JIANG Xiong(School of Chemistry and Chemical Engineering of Southwest Petroleum University,Chengdu 610500,China)
出处 《应用化工》 CSCD 北大核心 2018年第8期1587-1590,共4页 Applied chemical industry
基金 国家自然科学基金资助(41702391)
关键词 沥青 磺化 SEBS 封堵 asphalt sulfonation SEBS plugging
作者简介 胡正文(1981-),男,四川成都人,西南石油大学讲师,博士,主要从事油田化学品的研发工作。电话:028-83037364,E-mail:6638890@qq.com;通讯联系人:马丽华
  • 相关文献

参考文献7

二级参考文献39

共引文献68

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈