极化电位对铜系防污涂层性能的影响 预览

Effect of polarization potential on properties of copper-based antifouling coating
在线阅读 下载PDF
分享 导出
摘要 采用电化学阻抗谱研究了外加0.0、-0.7和-0.9V(相对于饱和甘汞电极)极化电位对铜系防污涂层在青岛海域海水中防护性能的影响,采用三维电子显微镜对涂层腐蚀形貌进行观察,以原子吸收分光光度计测量介质中铜元素的含量来表征防污剂(氧化亚铜)的溶解速率,并进行了6个月的实海试验。结果表明,极化电位加速了涂层的阴极剥离过程,明显降低了其防腐和防污性能。 The effect of polarization potential, i.e. 0.0,-0.7, or-0.9 V(vs. saturated calomel electrode), on protective property of copper-based antifouling coating in seawater around Qingdao was studied by electrochemical impedance spectroscopy. The surface corrosion morphology was observed using three-dimensional electron microscope. The dissolution rate of antifouling agent, i.e. copper(I) oxide, was characterized by determination of copper content in the medium by atomic absorption spectrophotometry. A real sea trial was conducted for 6 months. The results showed that the application of polarization potential accelerated the cathodic delamination of the coating and reduced its anticorrosion and antifouling properties greatly.
作者 方云辉 周开河 蔡辉 孙立三 刘志伟 王春婷 郑文茹 蒲吉斌 刘栓 李震 FANG Yun-hui;ZHOU Kai-he;CAI Hui;SUN Li-san;LIU Zhi-wei;WANG Chun-ting;ZHENG Wen-ru;PU Ji-bin;LIU Shuan;LI Zhen(Ningbo Power Supply Company,State Grid Zhejiang Electric Power Corporation,Ningbo 315201,China)
出处 《电镀与涂饰》 CAS CSCD 北大核心 2019年第2期76-81,共6页 Electroplating & Finishing
基金 青岛海洋科学与技术国家实验室2016年度开放基金(QNLM2016ORP0409) 国网浙江省电力公司科学技术项目(5211DS16001N,5211NB16000F)。
关键词 防污涂层 氧化亚铜 阴极保护 极化电位 海水 耐蚀性 antifouling coating copper(I) oxide cathodic protection polarization potential seawater corrosion resistance
作者简介 第一作者:方云辉(1982–),男,浙江诸暨人,高级工程师,主要从事金属腐蚀防护的研究;通信作者:刘栓(1986–),男,湖北钟祥人,博士,研究方向为腐蚀与防护。