FeCrAl铁素体不锈钢在压水堆水化学偏离工况下的应力腐蚀行为 预览

Stress Corrosion Behavior of FeCrAl Ferrite Stainless Steel under PWR Water Deviation Condition
在线阅读 下载PDF
收藏 分享 导出
摘要 采用慢应变速率拉伸(SSRT)试验方法,研究了FeCrAl铁素体不锈钢在偏离压水堆正常工况下的应力腐蚀行为。结果表明,在含有微量Cu^2+与Cl^-的高温水介质中,应变速率为2×10^-7s^-1时,FeCrAl铁素体不锈钢将发生显著的应力腐蚀开裂;其在含Cu^2+和Cl^-的高温水介质中的应力腐蚀开裂主要由点蚀导致。 Stress corrosion behavior of FeCrAl ferrite stainless steel under PWR water deviation condition was investigated by slow strain rate tensile (SSRT) tests. The results show that FeCrAl ferrite stainless steel is subject to stress corrosion cracking (SCC) at strain rate of 2×10 ^-7 s ^-1 , with the co-exist of Cu^2+ and Cl^- in water. SCC of FeCrAl ferrite stainless steel in high temperature water containing Cu^2+ and Cl^- is considered to result from pitting corrosion.
作者 肖婷 肖军 陈勇 周军 王辉 XIAO Ting;XIAO Jun;CHEN Yong;ZHOU Jun;WANG Hui(Science and Technology on Reactor Fuel and Materials Laboratory,Nuclear Power Institute of China, Chengdu 610213, China)
出处 《原子能科学技术》 EI CAS CSCD 北大核心 2019年第3期414-419,共6页 Atomic Energy Science and Technology
关键词 应力腐蚀开裂 FeCrAl铁素体不锈钢 慢应变速率拉伸 stress corrosion cracking FeCrAl ferrite stainless steel slow strain rate tensile
作者简介 肖婷(1994-),女(瑶族),湖南永州人,硕士研究生,核燃料循环与材料专业.
  • 相关文献

参考文献3

  • 1陈鹤鸣等编著..核反应堆材料腐蚀及其防护[M].北京:原子能出版社,1984:376.
  • 2舒俊..汽车排气系统用铁素体不锈钢耐蚀性能和成形性能的研究[D].上海交通大学,2013:
  • 3林震霞,邱绍宇,肖军,付正鸿,陈勇.Cl-和Cu2+对国产690合金应力腐蚀性能的影响[J].核动力工程,2015,36(1):50-54. 被引量:2

二级参考文献11

共引文献1

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈