复合模板剂对合成硅铝酸盐介孔材料的影响 预览

Effect of Composite Template on Synthetic Aluminosilicate Mesoporous Materials
在线阅读 下载PDF
收藏 分享 导出
摘要 以偏铝酸钠和水玻璃为导向剂,采用水热法在不同复合模板剂的条件下合成硅铝酸盐介孔材料。利用 X-射线衍射仪(XRD),扫描电子显微镜(SEM)及比表面积测定仪(N2 吸附/脱附)等对合成样品进行表征分析,研究了复合模板剂种类、添加量配比对合成的硅铝酸盐介孔材料的孔结构、形貌及性能参数的影响。结果表明,最佳复合模板剂为 F108、CTAB 和 CMC,确定 F108 加入量,CTAB与CMC 加入量的质量比值为 1∶0.3 时,合成材料的结构参数最优,孔径越大,磁滞损耗和介电损耗正切值也越大,吸波性能更好。 Aluminosilicate mesoporous materials were synthesized by hydrothermal method under different conditions of composite templating agent with sodium metaaluminate and water glass as guiding agents. The synthesized samples were characterized by X-ray diffractometry (XRD), scanning electron microscopy (SEM) and specific surface area analyzer (N 2 adsorption/desorption), and the composite templating agent type and addition ratio were synthesized. The effect of pore structure, morphology and performance parameters of aluminosilicate mesoporous materials. The results show that the best composite template is F108, CTAB and CMC, and the amount of F108 is determined. When the mass ratio of CTAB and CMC is 1∶0.3, the structural parameters of the composite are optimal, the larger the pore size, the hysteresis loss and the The electric loss tangent is also larger, and the absorbing performance is better.
作者 马志军 高静 张琪 苏文贵 Ma Zhijun;Gao Jing;Zhang Qi;Su Wengui(Liaoning Technical University, College of Mining, Fuxin, Liaoning 123000)
出处 《非金属矿》 CAS CSCD 北大核心 2019年第3期58-61,共4页 Non-metallic Mines
基金 国家自然科学基金(51372108)。
关键词 复合模板剂 硅铝酸盐 介孔材料 水热合成 吸波性能 composite templating agent aluminosilicate mesoporous material hydrothermal synthesis absorbing performance
作者简介 通信作者:马志军,E-mail:zhijunma0930@126.com。
  • 相关文献

参考文献5

二级参考文献127

共引文献21

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈