可见光、远红外与激光兼容隐身光子晶体薄膜 预览

Compatible Stealth Photonic Crystal for Visible Light,Far Infrared and Lasers
在线阅读 下载PDF
收藏 分享 导出
摘要 为了降低军事装备被可见光、红外或激光探测器发现的概率,研究了可见光、远红外与1.06μm及10.6μm激光兼容隐身光子晶体薄膜。基于光子晶体的“光子禁带”和“光子局域”的特性,利用传输矩阵理论设计了3种不同颜色的隐身光子晶体薄膜,然后利用真空电子束蒸发镀膜技术进行了制备,最后利用相关仪器测试并得到了微观截面图、可见光照片、远红外热像图和反射光谱。结果显示,3种薄膜微观层间结合致密,膜厚符合理论设计。可见光波段具有青、黄或紫的特征颜色,可以组合形成迷彩图案来分割可见光图像。远红外大气窗口(8~14μm)内发射率小于0.3,可以有效抑制远红外辐射。反射光谱中1.06μm及10.6μm处反射率分别为10%和40%左右,能够有效减弱入射激光的回波功率。 We studied a new type of stealth photonic crystal films compatible for visible,far infrared,1.06μm laser and 10.6μm laser,for the purpose of minimizing the threats to important military targets from visible,infrared and laser detectors.In this paper,firstly,three kinds of compatible stealth photonic crystals with different colors were designed and simulated by transfer matrix method(TMM),and then fabricated by vacuum electron beam evaporation coating technique.Finally,we tested them by using relevant instruments and obtained scanning electron microscope(SEM)photos,visible photos,infrared thermogram and reflectance spectrogram.The result shows that the bonding between layers of films is compact and the thicknesses conform to the theoretical design.The prepared photonic crystal films possess optical characteristics of cyan,yellow or violet,which can be used to form camouflage patterns to segment visible images.In addition,the average emissivity in 8-14μm far infrared atmospheric window is less than 0.3,which can effectively suppress far-infrared radiation.The reflectivity at wavelength of 1.06μm and 10.6μm keeps at about 10%and 40%,respectively,which will enormously reduce the reflected power of the incident lasers.
作者 王航 赵大鹏 张继魁 王成名 陈宗胜 刘瑞煌 时家明 WANG Hang;ZHAO Da-peng;ZHANG Ji-kui;WANG Cheng-ming;CHEN Zong-sheng;LIU Rui-huang;SHI Jia-ming(State Key Laboratory of Pulsed Power Laser Technology,College of Electronic Engineering,National University of Defense Technology,Hefei 230037,China;Hefei National Laboratory for Physical Sciences at The Microscale,University of Science and Technology of China,Heifei 230036,China)
出处 《发光学报》 EI CAS CSCD 北大核心 2019年第9期1079-1085,共7页 Chinese Journal of Luminescence
基金 国防预研项目(KY17Z003)资助。
关键词 光子晶体 可见光 远红外 激光 兼容隐身 photonic crystal visible light far Infrared laser compatible stealth
作者简介 王航(1994-),男,四川德阳人,硕士研究生,2017年于长春理工大学获得学士学位,主要从事光子晶体隐身材料方面的研究。E-mail:1192420338@qq.com;时家明(1966-),男,安徽巢湖人,博士,教授,博士生导师,1996年于中国科学院等离子体物理研究所获得博士学位,主要从事隐身与反隐身技术的研究。E-mail:shijiaming66@163.com。
  • 相关文献
投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈