碳钢表面腐蚀性自脆型去污剂制备及其性能 预览

Preparation and Properties of Corrosive Self-brittle Decontaminant on Carbon Steel Surface
在线阅读 下载PDF
收藏 分享 导出
摘要 通过二氧化硅和P(MMA-co-MAA)复合,并添加HNO 3等腐蚀剂制备了一种用于碳钢表面的腐蚀性自脆型去污剂。利用电化学测试、形貌观察、失重测试等方法研究了去污剂的性能。结果表明:去污剂具有良好的自脆性能;硝酸含量为0.5 mol/L、硼砂含量为0.01 mol/L时,去污剂对碳钢的腐蚀去污效果最佳;去污剂在碳钢表面产生了均匀的腐蚀层,去污剂涂膜厚度为2~4 mm时,平均腐蚀深度可达2.9~3.8μm。 In this study,a corrosive self-brittle decontaminant for carbon steel surface was prepared through the composite of silica and P(MMA-co-MAA)and the addition of HNO 3.The performances of prepared decontaminant were characterized by electrochemical test,morphology characterization and weightlessness test.The results show that the decontaminant has a good self-brittle property;The decontaminant containing 0.5 mol/L nitric acid and 0.01 mol/L borax performs the best corrosion decontamination effect on carbon steel surface;The decontaminant produces a uniform corrosion layer on the surface of carbon steel;The average corrosion depth of carbon steel reaches 2.9-3.8μm as the thickness of the decontaminant coating is 2-4 mm.
作者 刘星浩 李银涛 王善强 周元林 LIU Xinghao;LI Yintao;WANG Shanqiang;ZHOU Yuanlin(State Key Laboratory of Environmentally-friendly Energy Materials,School of Materials Science and Engineering,Southwest University of Science and Technology,Mianyang 621010,Sichuan,China;State Key Laboratory of NBC Protection for Civilian,Beijing 102205,China)
出处 《西南科技大学学报》 CAS 2019年第3期23-27,共5页 Journal of Southwest University of Science and Technology
基金 国家自然科学基金(11zg2119) 国民核生化灾害防护国家重点实验室基金项目(SKLNBC2018-16)。
关键词 碳钢 腐蚀性 自脆型去污剂 Carbon steel Corrosion Self-brittle decontaminant
作者简介 第一作者:刘星浩,男,硕士研究生;通信作者:李银涛,男,副研究员,研究方向为辐射防护材料,E-mail:liyintao@swust.edu.cn;通信作者:周元林,男,教授,研究方向为辐射防护材料,E-mail:zhouyuanlin@swust.edu.cn。
  • 相关文献

参考文献3

二级参考文献5

共引文献1

投稿分析

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈