Biodegradation Behavior of Coated As-Extruded Mg-Sr Alloy in Simulated Body Fluid
1
作者 Ming-Chun Zhao Ying-Chao Zhao +7 位作者 Deng-Feng Yin Shuo Wang Yong-Ming Shangguan Chao Liu Li-Li Tan Ci-Jun Shuai Ke Yang Andrej Atrens 《金属学报:英文版》 SCIE EI CAS CSCD 2019年第10期1195-1206,共12页
As-extruded Mg-Sr alloy, a kind of promising biodegradable biomedical material, was coated using micro-arc oxidation and also using a phosphate conversion coating. The corrosion behaviors were investigated using Hanks... As-extruded Mg-Sr alloy, a kind of promising biodegradable biomedical material, was coated using micro-arc oxidation and also using a phosphate conversion coating. The corrosion behaviors were investigated using Hanks' solution. The corrosion of the as-extruded Mg-Sr alloy became more serious with increasing immersion time;that is, the corrosion pits became more numerous, larger and deeper, The micro-arc oxidation coating and the phosphate conversion coating were effective in improving the corrosion resistance of the as-extruded Mg-Sr alloy. The micro-arc oxidation coating was much more effective. Moreover, the as-extruded Mg-Sr alloy and the coated as-extruded Mg-Sr alloy exhibited lower corrosion rates than the as-cast Mg-Sr alloy and the corresponding coated as-cast Mg-Sr alloy, indicating that the corrosion properties of the coated samples are dependent on their substrates. The finer microstructure of the substrate of the as-extruded condition corroded much slower. The corrosion resistance of the coated Mg-Sr alloy depended on the coating itself and on the microstructure of the substrate. 展开更多
关键词 Mg alloy Micro-arc OXIDATION COATING PHOSPHATE CONVERSION COATING BIODEGRADATION Corrosion resistance
成膜时间对AZ31B镁合金Mn-Y转化膜的影响
2
作者 邹忠利 薛同 +2 位作者 陈炜晔 陈荣飞 杨少林 《稀土》 EI CAS CSCD 北大核心 2019年第2期104-112,共9页
镁合金表面稀土盐转化膜是近些年发展起来的一种绿色环保的表面处理技术,本文采用了电子扫描显微镜(SEM)、析氢实验、电化学工作站及X射线能量色散光谱(EDS)考察了不同成膜时间对获得的Mn-Y转化膜的微观形貌、耐蚀性、半导体特性及组成... 镁合金表面稀土盐转化膜是近些年发展起来的一种绿色环保的表面处理技术,本文采用了电子扫描显微镜(SEM)、析氢实验、电化学工作站及X射线能量色散光谱(EDS)考察了不同成膜时间对获得的Mn-Y转化膜的微观形貌、耐蚀性、半导体特性及组成的影响。实验结果表明,随着成膜时间的增加,AZ31B镁合金表面逐渐生成一层转化膜,膜层呈泥巴状,当成膜时间为5 min时,基体表面的转化膜层最为密实。析氢实验结果显示,当成膜时间为5 min时,镁合金的析氢量最小,说明其耐蚀性最好;动电位极化曲线和电化学交流阻抗谱结果同样显示,随着成膜时间的增加,镁合金表面的耐蚀性不断增加,成膜时间为5 min的试样耐蚀性最好。Mott-Schottky曲线测试结果表明,镁合金表面膜层为n型半导体,5 min获得镁合金试样的施主浓度ND最小,平带电位Efb最正,耐蚀性能最好。EDS结果表明,化学转化膜的主要成分由锰、钇的磷酸盐和氧化物组成。 展开更多
关键词 钇盐 成膜时间 镁合金 转化膜 耐蚀性
金属表面无铬转化膜研究进展 预览
3
作者 卢勇 孙翠洁 何之源 《塑料助剂》 2019年第3期19-24,共6页
介绍了无机盐类转化膜、稀土类转化膜、植酸转化膜等多种无铬、环境友好型转化膜,及其在金属表面处理中的应用。分析了转化膜存在裂纹的原因,并分别介绍了用磷酸二氢盐进行后处理、溶胶-凝胶密封、转化膜复合三种提高转化膜耐蚀性和致... 介绍了无机盐类转化膜、稀土类转化膜、植酸转化膜等多种无铬、环境友好型转化膜,及其在金属表面处理中的应用。分析了转化膜存在裂纹的原因,并分别介绍了用磷酸二氢盐进行后处理、溶胶-凝胶密封、转化膜复合三种提高转化膜耐蚀性和致密度的后处理技术。 展开更多
关键词 金属 植酸 转化膜 防腐
在线阅读 下载PDF
稀土元素对镁合金锡酸盐转化膜性能的影响 预览
4
作者 于丽娜 邵忠财 戴诗行 《电镀与环保》 CAS CSCD 北大核心 2019年第2期46-50,共5页
研究了硝酸镧、硝酸铈、氧化钕对镁合金锡酸盐转化膜性能的影响。通过单因素试验,得出加入硝酸镧的镁合金锡酸盐化学转化的最佳配方为:锡酸钠30g/L,焦磷酸钠25g/L,乙酸钠7.0g/L,四硼酸钠10g/L,氢氧化钠6.0g/L,硝酸镧0.8g/L,温度70℃,时... 研究了硝酸镧、硝酸铈、氧化钕对镁合金锡酸盐转化膜性能的影响。通过单因素试验,得出加入硝酸镧的镁合金锡酸盐化学转化的最佳配方为:锡酸钠30g/L,焦磷酸钠25g/L,乙酸钠7.0g/L,四硼酸钠10g/L,氢氧化钠6.0g/L,硝酸镧0.8g/L,温度70℃,时间50min。最优配方下得到的膜层均匀平滑,结晶颗粒细小、分布均匀、大小均等,相成分为Mg、Al12Mg17、MgSn(OH)6、La(OH)3和La2O3。与加入氧化钕和硝酸铈的膜层相比,加入硝酸镧的膜层的自腐蚀电流密度最低,耐蚀性最好。 展开更多
关键词 锡酸盐 镁合金 稀土 转化膜
在线阅读 下载PDF
钼酸钠对AZ91D镁合金钒/锆复合转化膜性能的影响 预览
5
作者 刘玮 安成强 +1 位作者 郝建军 代肇一 《电镀与精饰》 CAS 北大核心 2019年第8期10-13,共4页
为了进一步提高镁合金钒/锆复合转化膜的耐蚀性,在优化后的钒锆酸盐转化液体系中加入添加剂钼酸钠。分别采用电化学工作站、扫描电子显微镜和能谱分析仪检测膜层耐蚀性、微观形貌及组成成分。实验证明,加入添加剂后,转化膜耐蚀性得到很... 为了进一步提高镁合金钒/锆复合转化膜的耐蚀性,在优化后的钒锆酸盐转化液体系中加入添加剂钼酸钠。分别采用电化学工作站、扫描电子显微镜和能谱分析仪检测膜层耐蚀性、微观形貌及组成成分。实验证明,加入添加剂后,转化膜耐蚀性得到很大提升,钼酸钠改变了转化膜的形貌并使得晶粒进一步细化,膜层更加致密均匀。加入4g/L钼酸钠的钒/锆复合转化膜的腐蚀电位正移至-1.4131V,腐蚀电流降至1.107×10^-5A,极化电阻增大到7503Ω,盐雾腐蚀时间9h。 展开更多
关键词 镁合金 钒/锆酸盐 添加剂 转化膜 钼酸钠
在线阅读 下载PDF
金属表面植酸转化膜研究进展 预览
6
作者 卢勇 冯辉霞 张晓芳 《材料导报》 EI CAS CSCD 北大核心 2019年第9期1455-1461,共7页
化学转化膜技术是金属物件表面处理中应用较为广泛的一项技术,可使金属物件得到较好的防护,可用于金属防腐、耐磨、减摩、涂装底层,其应用涉及汽车制造、家电以及五金构件加工等诸多行业。化学转化膜技术作为最常用的金属表面预处理技术... 化学转化膜技术是金属物件表面处理中应用较为广泛的一项技术,可使金属物件得到较好的防护,可用于金属防腐、耐磨、减摩、涂装底层,其应用涉及汽车制造、家电以及五金构件加工等诸多行业。化学转化膜技术作为最常用的金属表面预处理技术,因工艺简单、效果显著、沉淀均匀、成本低且膜的厚度易控制等优势而受到越来越多的关注。传统的铬酸盐和磷酸盐转化处理方法会对环境产生持久性危害,因而已逐步被绿色环保的方法取代。目前,金属表面绿色前处理技术的开发和应用已成为该领域十分重要的研究方向。经过十几年的努力,研究人员相继开发了各类环境友好型转化膜。本文针对无铬化学转化膜,从锆盐、钛盐、钒盐、钼酸盐、锡酸盐、铌盐和稀土元素类转化膜等的制备工艺、防腐蚀效果等方面阐述了无铬化学转化膜的研究进展。虽然,无铬转化新技术有一定的实践应用,但作为防腐蚀技术而言,单一使用该技术的效果并不理想,还需要与其他方法相结合并加以改进。本文重点分析了植酸转化膜的沉积机理、影响因素及改进技术发展。植酸是从植物中提取的无毒天然有机大分子,分子中含有能够与金属离子发生螯合作用的六个磷酸基,每个磷酸基中又有两个羟基和四个氧原子,可在较宽的pH值范围内与大多数二价及以上的金属离子螯合形成稳定的配合物。植酸作为金属表面化学转化膜成膜材料在金属腐蚀与防护领域的应用越来越广泛。大量研究结果表明,金属在植酸处理液中通过电化学反应,使金属表面的金属离子与植酸分子发生螯合作用,沉积形成植酸化学转化膜。植酸化学转化膜的研究涉及多种金属如镁合金、钢、铁等。本文通过分析植酸转化膜的制备过程,总结了影响转化膜表面形貌和耐蚀性的三个主要因素,即植酸的浓度、处理� 展开更多
关键词 金属 植酸 转化膜 防腐
在线阅读 免费下载
镀锌钢板表面氟锆酸盐/乙酰苯胺复合转化膜制备与性能研究
7
作者 马继辉 郭瑞光 钟萍 《材料保护》 CAS CSCD 北大核心 2019年第10期79-84,共6页
为了提高镀锌钢的耐蚀性能,以氟锆酸钾、乙酰苯胺为成膜物质,在镀锌钢表面制备了氟锆酸盐/乙酰苯胺有机无机复合转化膜。采用扫描电子显微镜(SEM)、能谱仪(EDS)、傅里叶变换红外光谱仪(FTIR)、电化学工作站、中性盐雾试验(NSS)对复合膜... 为了提高镀锌钢的耐蚀性能,以氟锆酸钾、乙酰苯胺为成膜物质,在镀锌钢表面制备了氟锆酸盐/乙酰苯胺有机无机复合转化膜。采用扫描电子显微镜(SEM)、能谱仪(EDS)、傅里叶变换红外光谱仪(FTIR)、电化学工作站、中性盐雾试验(NSS)对复合膜进行了分析测试。结果表明:含乙酰苯胺特征官能团的复合膜为无定形结构,膜厚7μm,由Zn,Zr,C,O,F元素组成。经转化处理后,试样的腐蚀电位增加了97 mV,腐蚀电流密度降低了1个数量级,耐中性盐雾时间达96 h,耐蚀性能显著增强。 展开更多
关键词 镀锌钢 氟锆酸钾 乙酰苯胺 转化膜 耐蚀性
添加剂对铝合金稀土转化膜的影响 预览
8
作者 崔永辉 邵忠财 +1 位作者 李学田 魏守强 《表面技术》 EI CAS CSCD 北大核心 2019年第5期225-231,共7页
目的寻找有效提高稀土转化膜性能的添加剂体系。方法采用电化学手段研究添加剂(硼酸、柠檬酸钠、磷酸钠、硅酸钠、氟化氢铵、氟化钠、草酸铵)对稀土转化膜的影响,对于具有积极作用的添加剂,使用响应面法进行复配,并优化配方。通过扫描... 目的寻找有效提高稀土转化膜性能的添加剂体系。方法采用电化学手段研究添加剂(硼酸、柠檬酸钠、磷酸钠、硅酸钠、氟化氢铵、氟化钠、草酸铵)对稀土转化膜的影响,对于具有积极作用的添加剂,使用响应面法进行复配,并优化配方。通过扫描电子显微镜(SEM)、能谱仪(EDS)和电化学测试对优化条件下制备的稀土转化膜性能进行表征。结果向基础转化液中加入氟化钠(NaF)、柠檬酸钠(Na3C6H5O7)和磷酸钠(Na3PO4)可以提高稀土转化膜的电化学性能。经过复配并优化配方,得到最优添加剂体系为0.68g/L氟化钠+0.80g/L磷酸钠。该配方可以抑制铝合金在转化液中的溶解,有利于铈元素的沉积,使铈的沉积量由5.01%提高到了9.60%。优化配方下制备出的膜层更加均匀致密,腐蚀电位提高了0.13 V,点滴时间可达122 s。XRD和EDS结果表明,膜层的主要成分为非晶态的铈锰氧化物。结论 0.68 g/L氟化钠+0.80g/L磷酸钠为最优添加剂配方。在优化体系中制得的稀土膜层的电化学性能得到了提升,表面更加均匀致密。 展开更多
关键词 铝合金 稀土 无铬钝化 耐蚀性 转化膜 电化学
在线阅读 免费下载
Monolithic crystalline silicon solar cells with SiNx layers doped with Tb3+ and Yb3+ rare-earth ions
9
作者 Ing-Song Yu Shao-Chun Wu +3 位作者 Lucile Dumont Julien Cardin Christophe Labbé Fabrice Gourbilleau 《中国稀土学报:英文版》 SCIE EI CAS CSCD 2019年第5期515-519,共5页
In this study, we propose the fabrication of monolithic crystalline silicon solar cells with Tb3+ and Yb3+-doped silicon nitride(SiNx) layers by low-cost screen-printing methods. The performances of c-Si solar cells c... In this study, we propose the fabrication of monolithic crystalline silicon solar cells with Tb3+ and Yb3+-doped silicon nitride(SiNx) layers by low-cost screen-printing methods. The performances of c-Si solar cells can be enhanced by rare-earth ions doped SiNx layers via the mechanism of spectrum conversion.These SiNx doped and codoped thin films were deposited by reactive magnetron co-sputtering and integrated as the antireflection coating layers in c-Si solar cells. The characterizations of SiNx, SiNx:Tb3+ tand SiNx:Tb3+-Yb3+ thin films were conducted by means of photoluminescence, Rutherford backscattering spectroscopy, Ellipsometry spectroscopy and Fourier transform infrared measurements. Their composition and refractive index was optimized to obtain good anti-reflection coating layer for c-Si solar cells.Transmission electron microscopy performs the uniform coatings on the textured emitter of c-Si solar cells. After the metallization process, we demonstrate monolithic c-Si solar cells with spectrum conversion layers, which lead to a relative increase by 1.34% in the conversion efficiency. 展开更多
关键词 Crystalline SILICON solar cell Spectrum conversion SILICON NITRIDE Down-shifting RARE-EARTH ion ANTI-REFLECTION coating
材料腐蚀与防护综合实验设计与实践 预览
10
作者 王志华 王明静 李小池 《实验技术与管理》 CAS 北大核心 2019年第2期93-95,共3页
将科研项目的研究成果应用于实验课程的教学,设计了采用化学浸泡法在不锈钢表面制备金色铈盐转化膜的综合实验,并对制备的转化膜进行性能测试,使学生在实验过程中掌握制备化学转化膜的基本方法,掌握材料防腐的机理及措施,了解SEM、XRD... 将科研项目的研究成果应用于实验课程的教学,设计了采用化学浸泡法在不锈钢表面制备金色铈盐转化膜的综合实验,并对制备的转化膜进行性能测试,使学生在实验过程中掌握制备化学转化膜的基本方法,掌握材料防腐的机理及措施,了解SEM、XRD、电化学工作站等测试方法,提高分析实验数据的综合能力,激发学生的创新思维。 展开更多
关键词 综合实验 材料腐蚀与防护 转化膜
在线阅读 下载PDF
硝酸铈对镁合金锌、锰系磷酸盐转化膜性能的影响 预览
11
作者 张瑜 赵佳新 +1 位作者 代永祺 邵忠财 《电镀与环保》 CAS CSCD 北大核心 2019年第4期58-61,共4页
研究了硝酸铈对镁合金锌、锰系磷酸盐转化膜性能的影响。通过单因素试验得出:制备锌、锰系磷酸盐转化膜时,硝酸铈的最佳质量浓度分别为0.3 g/L和0.2 g/L。与锌系磷酸盐转化膜相比,锰系磷酸盐转化膜更加光滑致密,膜层中Ce的质量分数较高... 研究了硝酸铈对镁合金锌、锰系磷酸盐转化膜性能的影响。通过单因素试验得出:制备锌、锰系磷酸盐转化膜时,硝酸铈的最佳质量浓度分别为0.3 g/L和0.2 g/L。与锌系磷酸盐转化膜相比,锰系磷酸盐转化膜更加光滑致密,膜层中Ce的质量分数较高,耐蚀性更好。 展开更多
关键词 稀土 镁合金 转化膜 耐蚀性
在线阅读 下载PDF
不同稀土元素对镁合金钼酸盐转化膜耐蚀性的影响 预览
12
作者 杨欣然 张伟强 《电镀与环保》 CAS CSCD 北大核心 2019年第2期25-27,共3页
研究了硝酸铈、氧化钕和硝酸镧对镁合金钼酸盐转化膜耐蚀性的影响。通过单因素试验,得出添加氧化钕的镁合金钼酸盐化学转化的最佳配方为:钼酸铵25g/L,硝酸钠1.5g/L,硝酸锰1.0g/L,柠檬酸1.5g/L,氧化钕0.4g/L,pH值5,温度60℃,时间30min。... 研究了硝酸铈、氧化钕和硝酸镧对镁合金钼酸盐转化膜耐蚀性的影响。通过单因素试验,得出添加氧化钕的镁合金钼酸盐化学转化的最佳配方为:钼酸铵25g/L,硝酸钠1.5g/L,硝酸锰1.0g/L,柠檬酸1.5g/L,氧化钕0.4g/L,pH值5,温度60℃,时间30min。最佳配方下得到的膜层均匀平滑,结晶颗粒细小、分布均匀、大小均等。添加氧化钕的钼酸盐转化膜的自腐蚀电流密度最低,耐蚀性最好。 展开更多
关键词 镁合金 钼酸盐 转化膜 稀土
在线阅读 下载PDF
EDTA对镁合金锡酸盐转化膜耐蚀性的影响 预览
13
作者 朱宏达 管秀荣 邵忠财 《电镀与环保》 CAS CSCD 北大核心 2019年第5期45-47,共3页
研究了EDTA对镁合金锡酸盐转化膜耐蚀性的影响。首先,采用硫酸铜点滴试验、盐水浸泡试验和电化学试验测试了锡酸盐转化膜的耐蚀性;然后,分别采用金相显微镜和扫描电镜观察了锡酸盐转化膜的金相形貌和表面形貌;最后,采用X射线衍射仪分析... 研究了EDTA对镁合金锡酸盐转化膜耐蚀性的影响。首先,采用硫酸铜点滴试验、盐水浸泡试验和电化学试验测试了锡酸盐转化膜的耐蚀性;然后,分别采用金相显微镜和扫描电镜观察了锡酸盐转化膜的金相形貌和表面形貌;最后,采用X射线衍射仪分析了锡酸盐转化膜的相组成。结果表明:EDTA不仅能提高锡酸盐转化膜的耐蚀性,还能改善锡酸盐转化膜的形貌质量。由XRD分析得出,锡酸盐转化膜的相组成为Mg、Al12Mg7和MgSn(OH)6. 展开更多
关键词 镁合金 EDTA 锡酸盐 转化膜
在线阅读 下载PDF
水性高性能铁锈转化剂的制备及性能研究 预览
14
作者 山海强 杨小刚 金思毅 《青岛科技大学学报:自然科学版》 CAS 2018年第6期71-76,共6页
对铁锈转化剂配方进行了定性、定量筛选试验,确定了最佳添加剂种类及浓度,并对形成的转化膜性能进行了研究。通过实验确定了转化剂前处理液成分及含量:1%锌粉,1%乌洛托品,10%甘油,其余为水;转化剂后处理液成分及含量:45%多聚磷酸,3%单宁... 对铁锈转化剂配方进行了定性、定量筛选试验,确定了最佳添加剂种类及浓度,并对形成的转化膜性能进行了研究。通过实验确定了转化剂前处理液成分及含量:1%锌粉,1%乌洛托品,10%甘油,其余为水;转化剂后处理液成分及含量:45%多聚磷酸,3%单宁酸,5%硫酸锌,5%乙酸,其余为水。电化学测试结果表明:涂铁锈转化剂后的样片拟合的腐蚀电流变小,防腐能力得到提高。通过金相显微分析、扫描电子显微镜图像分析观察到:转化膜表面平整、致密。由能谱仪测试得到:转化膜中的主要元素为C、O、P、Fe、Zn;通过附着力测试表明:铁锈转化后形成的转化膜附着力较好。 展开更多
关键词 腐蚀 铁锈转化剂 转化膜 电化学分析
在线阅读 下载PDF
镁合金电化学转化膜的组成及反应机理 预览 被引量:1
15
作者 刘志江 朱卫国 《表面技术》 CSCD 北大核心 2018年第7期209-213,共5页
目的更好地开展镁合金防腐蚀研究,提高其耐蚀性。方法利用电化学法制备镁合金磷化膜,通过单因素条件实验研究电流密度、温度以及时间对反应过程的影响,得出制备最佳方案。通过X荧光光谱仪(EDX)、X射线衍射仪(XRD)及电化学测试等现代检... 目的更好地开展镁合金防腐蚀研究,提高其耐蚀性。方法利用电化学法制备镁合金磷化膜,通过单因素条件实验研究电流密度、温度以及时间对反应过程的影响,得出制备最佳方案。通过X荧光光谱仪(EDX)、X射线衍射仪(XRD)及电化学测试等现代检测技术对镁合金电化学膜微观结构、沉积速率等进行测试,得出制备的转化膜组成成分的定性及半定量分析结果,以此推断镁合金电化学转化膜的生成机理。结果电化学法制备镁合金磷化膜的最佳工艺条件为:电流密度0.5A/dm2,温度30℃,反应时间5min。EDX分析结果显示,磷化膜主要成分为Mg、P、Zn,其质量分数分别为11.017%、2.105%、28.534%。结论电化学转化膜的主要化学成分为Mg、P、Zn,还有少量其他成分,如Al、S、Ca、Mn、Ni、Cu。腐蚀机理复杂,不确定性较大。镁合金磷化膜主要由结晶型磷化锌、磷化铝、锌镁金属磷化夹杂物和单质Zn组成,并且还有少量的其他化合物。 展开更多
关键词 镁合金 电化学磷化 转化膜 反应机理
在线阅读 免费下载
不同添加剂对镁合金磷酸盐-高锰酸钾转化膜耐蚀性的影响 预览 被引量:1
16
作者 戴诗行 邵忠财 《电镀与环保》 CSCD 北大核心 2018年第5期46-49,共4页
研究了EDTA、柠檬酸、酒石酸、氟化钠对磷酸盐高锰酸钾转化膜的影响。采用金相显微镜观察了转化膜的微观形貌,并通过电化学测试和全浸蚀试验研究了转化膜的耐蚀性。结果表明:化学转化处理提高了镁合金的耐蚀性,而且不同添加剂对转化... 研究了EDTA、柠檬酸、酒石酸、氟化钠对磷酸盐高锰酸钾转化膜的影响。采用金相显微镜观察了转化膜的微观形貌,并通过电化学测试和全浸蚀试验研究了转化膜的耐蚀性。结果表明:化学转化处理提高了镁合金的耐蚀性,而且不同添加剂对转化膜耐蚀性的提高效果不一样。其中复合添加剂对镁合金耐蚀性的提高效果更为显著,最优配方为:磷酸二氢铵80 g/L,高锰酸钾20g/L,酒石酸0.5 g/L。氟化钠0.4 g/L,温度35 ℃,时问25 min。 展开更多
关键词 磷酸盐 镁合金 转化膜 添加剂
在线阅读 下载PDF
镁合金表面转化膜预处理工艺的研究进展 预览 被引量:1
17
作者 宫宁 卜红梅 +3 位作者 任祥龙 齐建涛 李焰 王振波 《材料导报》 CSCD 北大核心 2018年第A02期315-321,共7页
本文阐述了镁合金腐蚀的原因、机理、类型及其腐蚀特点,总结了磷酸盐-高锰酸盐转化膜、稀土金属盐转化膜、氟锆酸盐转化膜和钒酸盐转化膜等转化膜预处理工艺的主要优缺点,重点评述了转化膜预处理的耐蚀性能和环境友好性能,并对其发展进... 本文阐述了镁合金腐蚀的原因、机理、类型及其腐蚀特点,总结了磷酸盐-高锰酸盐转化膜、稀土金属盐转化膜、氟锆酸盐转化膜和钒酸盐转化膜等转化膜预处理工艺的主要优缺点,重点评述了转化膜预处理的耐蚀性能和环境友好性能,并对其发展进行了展望。 展开更多
关键词 镁合金 转化膜 腐蚀 环境友好
在线阅读 免费下载
镁合金锌系磷酸盐化学转化膜的研究 预览 被引量:3
18
作者 邵忠财 戴诗行 魏守强 《表面技术》 CSCD 北大核心 2018年第4期133-139,共7页
目的 优化镁合金锌系磷酸盐化学转化膜的制备工艺。方法 制备锌系磷酸盐化学转化膜,采用点滴实验、电化学测试对化学转化膜进行耐蚀性评价,并通过激光共聚焦显微镜、扫描电子显微镜(SEM)和X射线衍射仪(XRD)对膜层进行表征,研究主盐... 目的 优化镁合金锌系磷酸盐化学转化膜的制备工艺。方法 制备锌系磷酸盐化学转化膜,采用点滴实验、电化学测试对化学转化膜进行耐蚀性评价,并通过激光共聚焦显微镜、扫描电子显微镜(SEM)和X射线衍射仪(XRD)对膜层进行表征,研究主盐、温度和添加剂对镁合金锌系磷酸盐化学转化膜的影响。结果 转化溶液中氧化锌、磷酸、氟化钠、酒石酸钠的浓度对转化膜的耐蚀性和膜厚具有较大影响,在一定浓度范围内,转化膜的耐蚀性随浓度的增加而增大。转化膜耐蚀性随温度的升高先增加后下降,50℃时点滴时间达到59 s,膜层相对致密,缝隙较小。选取的添加剂中,EDTA能明显提高膜层的耐蚀性,膜层均匀致密,加入0.3 g/L EDTA的转化膜的腐蚀电位比未加添加剂的转化膜正移0.05 V,点滴时间提高到68 s。镁合金锌系磷酸盐转化膜主要成分为Zn3(PO4)2+Zn2Mg(PO4)2+AlPO4+Al(12)Mg(17)。转化膜的电化学阻抗半径大,自腐蚀电流密度低(2.594×10^-6 A/cm^2),腐蚀电位正移较明显,耐蚀性更好。转化膜粗糙度小(2.396μm),平整光滑。结论 镁合金锌系磷酸盐转化最优配方及工艺为:氧化锌2.0 g/L,磷酸12 g/L,氟化钠1.0 g/L,酒石酸钠4.0 g/L,EDTA 0.3 g/L,转化温度50℃,转化时间20 min。转化溶液加入EDTA后,能够明显提高转化膜的耐蚀性。 展开更多
关键词 镁合金 转化膜 磷酸盐 耐蚀性 温度 电化学
在线阅读 免费下载
镁合金静电喷雾喷嘴表面镀层组织与性能研究
19
作者 朱彤珺 王莹 《铸造技术》 北大核心 2017年第10期2408-2411,共4页
通过在镁基喷嘴表面制备锡酸盐转化膜和化学镀层,对比分析了镁基材、转化膜和镀层的显微形貌、物相组成、腐蚀形貌和电化学性能。结果表明,锡酸盐转化前的试样表面物相由α-Mg和Mg_(17)Al_(12)组成,锡酸盐转化后表面膜层由α-Mg、Mg... 通过在镁基喷嘴表面制备锡酸盐转化膜和化学镀层,对比分析了镁基材、转化膜和镀层的显微形貌、物相组成、腐蚀形貌和电化学性能。结果表明,锡酸盐转化前的试样表面物相由α-Mg和Mg_(17)Al_(12)组成,锡酸盐转化后表面膜层由α-Mg、Mg_(17)Al_(12)和Mg Sn O_3·3H_2O组成;化学镀层的表面腐蚀形貌相对锡酸盐转化膜更轻,而采用45 g/L Ni SO_4·6H_2O和60 g/L Na H_2PO_2的镀层没有发生明显腐蚀。 展开更多
关键词 镁基材 转化膜 表面镀层 显微形貌 耐腐蚀
金属表面无铬钝化研究进展 预览 被引量:2
20
作者 纪忆 张永海 《电镀与涂饰》 CSCD 北大核心 2017年第12期655-659,共5页
从原理、性能、工艺等方面总结了金属表面无铬钝化技术的发展现状。重点介绍了近年来报道中可行性较高的无铬复合钝化液的配方及工艺参数,阐述了未来无铬钝化技术的发展趋势。
关键词 金属 无铬钝化 转化膜 硅烷偶联剂 树脂 有机-无机杂化物
在线阅读 下载PDF