三甲基间苯二胺型聚酰亚胺薄膜的制备与性能研究 认领 被引量:1

Preparation and Properties Study of Polyimide Film Based on Trimethyl-m-phenylenediamine
在线阅读 下载PDF
收藏 分享 导出
摘要 采用2,4,6-三甲基间苯二胺(TMmPDA)、4,4′-二氨基二苯醚(DADPE)和3,3′,4,4′-四羧基联苯二酐(BP-DA)为原料,合成得到了三甲基间苯二胺型聚酰胺酸(TMPAA)溶液,经涂膜、热亚胺化,制得了三甲基间苯二胺型聚酰亚胺(TMPI)薄膜,并对其性能进行了研究。结果表明:三甲基间苯二胺型聚酰亚胺薄膜具有良好的光学透明性、较低的介质损耗、良好的疏水性能,比含羧基聚酰亚胺薄膜具有更好的柔韧性和更高的断裂拉伸强度。 Using 2,4,6-trimethyl-m-phenylenediamine (TMmPDA), 4,4'-diaminodiphenyl ether (DADPE) and 3,3',4,4'-tetracarboxylic biphenyl dianhydride (BPDA) as raw material, a polyamide acid (TMPAA) solution was synthesized by condensation reaction, and the corresponding polyimide (TMPI) film was pre- pared by thermal imidization, and its properties were studied. The results show that the TMP! film has good optical transparency, low dielectric loss and low water absorption and has better flexibility and high- er breaking tensile strength than that of the polyimide film containing carboxyl.
作者 虞鑫海 虞静远 许梅芳 郑秀秀 徐永芬 钱明球 赵炯心 Yu Xinhai, Yu Jingyuan, Xu Meifang, Zheng Xiuxiu, Xu Yongfen, Qian Mingqiu, Zhao Jiongxin (1. Department of Applied Chemistry, Donghua University, Shanghai 201620, China," 2. Sinopec tTzheng Chemical Fiber Co., Ltd., ITzheng 211900, China)
出处 《绝缘材料》 CAS 北大核心 2013年第3期60-63,共4页 Insulating Materials
关键词 2 4 6-三甲基间苯二胺 4 4′-二氨基二苯醚 3 3′ 4 4′-四羧基联苯二酐 聚酰亚胺薄膜 性能 2,4,6-trimethyl-m-phenylenediamine 4,4'-diaminodiphenyl ether 3,3 ',4,4'-tetracarboxylic biphe- nyl dianhydride polyimide film properties
  • 相关文献

参考文献23

二级参考文献70

共引文献80

同被引文献8

引证文献1

二级引证文献2

维普数据出版直通车
今日学术
投稿分析
职称考试

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部 意见反馈